Interior crystallographic plane induced cracking behavior of Ni-based superalloy in high-temperature and vacuum environment

Engineering

• Schmids Factor 100%
• Cracking Behavior 100%
• Induced Cracking 100%
• Transmissions 50%
• Activation Energy 50%
• Microstructure 50%
• Crack Initiation 50%
• Crack Growth 50%
• Microcracks 50%
• Micro Crack 50%
• Mechanical Fatigue Test 50%
• Focused Ion Beam 50%
• Energy Dispersive Spectrometer 50%
• Single Plane 50%

Material Science

• Nickel-Based Superalloys 100%
• Scanning Electron Microscopy 50%
• Activation Energy 50%
• Focused Ion Beam 50%
• Electron Backscatter Diffraction 50%
• Crack Growth 50%
• Crack Initiation 50%
• Microcracks 50%