Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

Lichen Zhang; Shuo Wang; Xing Su; Xiaodong Li; Meishuai Zou

doi:10.1016/j.partic.2022.08.008

Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

Lichen Zhang, Shuo Wang, Xing Su, Xiaodong Li^*, Meishuai Zou^*

^*此作品的通讯作者

材料学院

Beijing Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

22 引用（Scopus）

摘要

The dense alumina shell on the surface of aluminum powder will hinder the combustion of aluminum powder and increase its ignition temperature. In this study, the aluminum oxide shell layer on the surface of aluminum powder was removed with hydrofluoric acid by one-pot method, and 3-Perfluorohexyl-1, 2-epoxypropane (PFHP) (F₃C(CF₂)₅CH₂C₂H₃O) was coated to form a uniform and controllable core-shell Al@PFHP. The core-shell Al@PFHP showed better thermal reaction and ignition performance. The exothermic enthalpy of Al@0.15 PFHP was increased by about 1.9 times, with lower ignition temperature (reduced by about 140 °C) and longer burning duration (increased by about 1.5 times) after coating with PFHP, compared with raw aluminum powder. In addition, the formation of PFHP coating shell can effectively improve the hydrophobicity and corrosion resistance of aluminum powder.

源语言	英语
页（从-至）	62-70
页数	9
期刊	Particuology
卷	77
DOI	https://doi.org/10.1016/j.partic.2022.08.008
出版状态	已出版 - 6月 2023

访问文件

10.1016/j.partic.2022.08.008

其它文件与链接

链接到 Scopus 的出版物

引用此

Zhang, L., Wang, S., Su, X., Li, X., & Zou, M. (2023). Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder. Particuology, 77, 62-70. https://doi.org/10.1016/j.partic.2022.08.008

@article{a403218bc1074a17beb3e8648929cdf3,

title = "Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder",

abstract = "The dense alumina shell on the surface of aluminum powder will hinder the combustion of aluminum powder and increase its ignition temperature. In this study, the aluminum oxide shell layer on the surface of aluminum powder was removed with hydrofluoric acid by one-pot method, and 3-Perfluorohexyl-1, 2-epoxypropane (PFHP) (F3C(CF2)5CH2C2H3O) was coated to form a uniform and controllable core-shell Al@PFHP. The core-shell Al@PFHP showed better thermal reaction and ignition performance. The exothermic enthalpy of Al@0.15 PFHP was increased by about 1.9 times, with lower ignition temperature (reduced by about 140 °C) and longer burning duration (increased by about 1.5 times) after coating with PFHP, compared with raw aluminum powder. In addition, the formation of PFHP coating shell can effectively improve the hydrophobicity and corrosion resistance of aluminum powder.",

keywords = "2-Epoxypropane, 3-Perfluorohexyl-1, Aluminum powder, Combustion, Core-shell",

author = "Lichen Zhang and Shuo Wang and Xing Su and Xiaodong Li and Meishuai Zou",

note = "Publisher Copyright: {\textcopyright} 2022",

year = "2023",

month = jun,

doi = "10.1016/j.partic.2022.08.008",

language = "English",

volume = "77",

pages = "62--70",

journal = "Particuology",

issn = "1674-2001",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

AU - Zhang, Lichen

AU - Wang, Shuo

AU - Su, Xing

AU - Li, Xiaodong

AU - Zou, Meishuai

PY - 2023/6

Y1 - 2023/6

N2 - The dense alumina shell on the surface of aluminum powder will hinder the combustion of aluminum powder and increase its ignition temperature. In this study, the aluminum oxide shell layer on the surface of aluminum powder was removed with hydrofluoric acid by one-pot method, and 3-Perfluorohexyl-1, 2-epoxypropane (PFHP) (F3C(CF2)5CH2C2H3O) was coated to form a uniform and controllable core-shell Al@PFHP. The core-shell Al@PFHP showed better thermal reaction and ignition performance. The exothermic enthalpy of Al@0.15 PFHP was increased by about 1.9 times, with lower ignition temperature (reduced by about 140 °C) and longer burning duration (increased by about 1.5 times) after coating with PFHP, compared with raw aluminum powder. In addition, the formation of PFHP coating shell can effectively improve the hydrophobicity and corrosion resistance of aluminum powder.

AB - The dense alumina shell on the surface of aluminum powder will hinder the combustion of aluminum powder and increase its ignition temperature. In this study, the aluminum oxide shell layer on the surface of aluminum powder was removed with hydrofluoric acid by one-pot method, and 3-Perfluorohexyl-1, 2-epoxypropane (PFHP) (F3C(CF2)5CH2C2H3O) was coated to form a uniform and controllable core-shell Al@PFHP. The core-shell Al@PFHP showed better thermal reaction and ignition performance. The exothermic enthalpy of Al@0.15 PFHP was increased by about 1.9 times, with lower ignition temperature (reduced by about 140 °C) and longer burning duration (increased by about 1.5 times) after coating with PFHP, compared with raw aluminum powder. In addition, the formation of PFHP coating shell can effectively improve the hydrophobicity and corrosion resistance of aluminum powder.

KW - 2-Epoxypropane

KW - 3-Perfluorohexyl-1

KW - Aluminum powder

KW - Combustion

KW - Core-shell

UR - http://www.scopus.com/inward/record.url?scp=85141527649&partnerID=8YFLogxK

U2 - 10.1016/j.partic.2022.08.008

DO - 10.1016/j.partic.2022.08.008

M3 - Article

AN - SCOPUS:85141527649

SN - 1674-2001

VL - 77

SP - 62

EP - 70

JO - Particuology

JF - Particuology

ER -

Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

摘要

访问文件

其它文件与链接

指纹

引用此