On the dynamic failure mechanism of Vit-1 bulk metallic glass: Coupling effects of pre-made damage and strain rate

Yang Han, Zejian Xu*, P. J. Tan, Mengyu Su, Jianfei Li, Fenglei Huang

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

摘要

To clarify the two distinct effects and the underlying physical mechanisms of pre-made damage on the failure strength of bulk metallic glass (BMG), i.e. strengthening or weakening, the influence of axial pre-compression on the dynamic failure of Vit-1 BMG are investigated experimentally. Quasi-static and dynamic compression tests were conducted on pre-compressed BMG specimens for a wide range of nominal strain rates between 0.001 s−1 to 6000 s−1. The focus is on the coupled effects of pre-compression and strain rate on the dynamic failure stress. Two contrasting mechanisms were identified that influence how the pre-made shear bands affect the propagation of cracks under different strain rates. It will be shown that the dynamic failure stress exhibits a transition from strengthening to knockdown with increasing strain rate; and, that the extent of these strengthening and knockdown effects depends on the pre-compression strain level. Finally, a failure model that captures the effects of both strain rate and pre-made damage is proposed.

源语言英语
文章编号147522
期刊Materials Science and Engineering: A
919
DOI
出版状态已出版 - 1月 2025

指纹

探究 'On the dynamic failure mechanism of Vit-1 bulk metallic glass: Coupling effects of pre-made damage and strain rate' 的科研主题。它们共同构成独一无二的指纹。

引用此