Biaxially textured yttria stabilized zirconia (YSZ) thin films, were deposited on glass substrates by ion beam assisted deposition method with different deposition time. As contrasts, films were also fabricated without assisting ion beam. The orientation properties of the films were characterized by X-ray diffraction. A comparative study shows that there is a competition between (0 0 1) and (0 1 1) alignments during the growth process. Assisting ions make the films (0 0 1)-advantaged and biaxially textured. The competitive growth and the orientation development are explained by selective resputtering and anisotropic damage on growing films induced by assisting ions.
| 源语言 | 英语 |
|---|---|
| 页（从-至） | 622-625 |
| 页数 | 4 |
| 期刊 | Physica C: Superconductivity and its Applications |
| 卷 | 470 |
| 期 | 15-16 |
| DOI | |
| 出版状态 | 已出版 - 1 8月 2010 |
指纹
探究 'A competition between (0 0 1) and (0 1 1) alignments in yttria stabilized zirconia thin films fabricated by ion beam assisted deposition' 的科研主题。它们共同构成独一无二的指纹。引用此
Wang, Z., Yan, B. J., Feng, F., Chen, H., Shi, K., & Han, Z. (2010). A competition between (0 0 1) and (0 1 1) alignments in yttria stabilized zirconia thin films fabricated by ion beam assisted deposition. Physica C: Superconductivity and its Applications, 470(15-16), 622-625. https://doi.org/10.1016/j.physc.2010.06.002