AU - Gan, Junyan
AU - Jin, Shaohua
AU - Chen, Yu
N1 - Publisher Copyright:
© 2021 Institute of Physics Publishing. All rights reserved.
PY - 2021/10/28
Y1 - 2021/10/28
N2 - Different types of TKX-50/PBA-I composite materials were prepared by the solution-water suspension method, and the influence of the content of anionic groups on the coating effect was explored by SEM, FT-IR, XPS and TGA. The results showed that PBA-I were successfully coated on the crystal surface of TKX-50, and the content of anionic group -COOH increased, which was conducive to the coating effect of the bonding agent on TKX-50. Among the different anionic bonding agents, PBA-I-3 had the best coating effect.
AB - Different types of TKX-50/PBA-I composite materials were prepared by the solution-water suspension method, and the influence of the content of anionic groups on the coating effect was explored by SEM, FT-IR, XPS and TGA. The results showed that PBA-I were successfully coated on the crystal surface of TKX-50, and the content of anionic group -COOH increased, which was conducive to the coating effect of the bonding agent on TKX-50. Among the different anionic bonding agents, PBA-I-3 had the best coating effect.
UR - http://www.scopus.com/inward/record.url?scp=85119168841&partnerID=8YFLogxK
U2 - 10.1088/1742-6596/2044/1/012056
DO - 10.1088/1742-6596/2044/1/012056
M3 - Conference article
AN - SCOPUS:85119168841
SN - 1742-6588
VL - 2044
JO - Journal of Physics: Conference Series
JF - Journal of Physics: Conference Series
IS - 1
M1 - 012056
T2 - 2nd International Conference on Advanced Materials and Intelligent Manufacturing, ICAMIM 2021
Y2 - 20 August 2021 through 22 August 2021
ER -