Synthesis and characterization of Mg-based bulk metallic glass

Jie Qiong Li; Lu Wang; Hai Feng Zhang; Guang Shu Lu; Zhuang Qi Hu; Hong Nian Cai

Synthesis and characterization of Mg-based bulk metallic glass

Jie Qiong Li^*, Lu Wang, Hai Feng Zhang, Guang Shu Lu, Zhuang Qi Hu, Hong Nian Cai

^*此作品的通讯作者

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

Bulk metallic glass of Mg65Cu20Ag5Gd10 with the maximal diameter of 12 mm was synthesized successfully by copper mould casting. Its structure, thermal stability, mechanical properties and fracture surfaces were studied. Results indicate that Mg65Cu20Ag5Gd10 exhibits high thermal stability and glass forming capability. The compressive fracture strength and elastic strain limit of the metallic glass reach about 895 MPa and 2.35%, respectively.

源语言	英语
页（从-至）	125-128
页数	4
期刊	Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology
卷	41
期	11
出版状态	已出版 - 11月 2009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{3e06b667ad0747d5b93a61d16d06d7bd,

title = "Synthesis and characterization of Mg-based bulk metallic glass",

abstract = "Bulk metallic glass of Mg65Cu20Ag5Gd10 with the maximal diameter of 12 mm was synthesized successfully by copper mould casting. Its structure, thermal stability, mechanical properties and fracture surfaces were studied. Results indicate that Mg65Cu20Ag5Gd10 exhibits high thermal stability and glass forming capability. The compressive fracture strength and elastic strain limit of the metallic glass reach about 895 MPa and 2.35%, respectively.",

keywords = "Bulk metallic glass, Glass forming capability, Thermal stability",

author = "Li, {Jie Qiong} and Lu Wang and Zhang, {Hai Feng} and Lu, {Guang Shu} and Hu, {Zhuang Qi} and Cai, {Hong Nian}",

year = "2009",

month = nov,

language = "English",

volume = "41",

pages = "125--128",

journal = "Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology",

issn = "0367-6234",

publisher = "Harbin Institute of Technology",

number = "11",

}

TY - JOUR

T1 - Synthesis and characterization of Mg-based bulk metallic glass

AU - Li, Jie Qiong

AU - Wang, Lu

AU - Zhang, Hai Feng

AU - Lu, Guang Shu

AU - Hu, Zhuang Qi

AU - Cai, Hong Nian

PY - 2009/11

Y1 - 2009/11

N2 - Bulk metallic glass of Mg65Cu20Ag5Gd10 with the maximal diameter of 12 mm was synthesized successfully by copper mould casting. Its structure, thermal stability, mechanical properties and fracture surfaces were studied. Results indicate that Mg65Cu20Ag5Gd10 exhibits high thermal stability and glass forming capability. The compressive fracture strength and elastic strain limit of the metallic glass reach about 895 MPa and 2.35%, respectively.

AB - Bulk metallic glass of Mg65Cu20Ag5Gd10 with the maximal diameter of 12 mm was synthesized successfully by copper mould casting. Its structure, thermal stability, mechanical properties and fracture surfaces were studied. Results indicate that Mg65Cu20Ag5Gd10 exhibits high thermal stability and glass forming capability. The compressive fracture strength and elastic strain limit of the metallic glass reach about 895 MPa and 2.35%, respectively.

KW - Bulk metallic glass

KW - Glass forming capability

KW - Thermal stability

UR - http://www.scopus.com/inward/record.url?scp=74949100544&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:74949100544

SN - 0367-6234

VL - 41

SP - 125

EP - 128

JO - Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology

JF - Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology

IS - 11

ER -

Synthesis and characterization of Mg-based bulk metallic glass

摘要

其它文件与链接

指纹

引用此