Preparation and characterization of organic-inorganic hybrid ZrOC/PF aerogel used as high-temperature insulator

Sue Ren, li Hu, Xiutao Li, Jinpeng Fan, Jun Liang*

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

11 引用 (Scopus)

摘要

Organic-inorganic hybrid ZrOC/PF aerogel composite is successfully prepared via one sol-gel polymerization process, using PF and ZrOC sols as precursor, respectively. SEM, BET, FT-IR, and XPS measurements are used to investigate the effect of the mass ratio of ZrOC to PF on physical, microstructure, and thermal properties of the composite aerogels. Results show that the aerogels exhibit relative low density (0.258–0.332 g/cm3), relative high compressive strength (0.32–1.40 MPa), and low thermal conductivity (0.0466–0.0660 W/m·K). SEM images demonstrated that the particles are composed of the tangled clusters of the PF and ZrOC and the particle size ranges from a dozen nm to tens of nm, up to several microns. XPS results indicate that elements C, O, and Zr in the samples are based on C–C and Zr–O valences band binding, respectively. The ZrOC/PF aerogel with excellent physical property and potential high-temperature resistance may be used in aerospace in the near future.

源语言英语
页(从-至)6326-6332
页数7
期刊Ceramics International
46
5
DOI
出版状态已出版 - 1 4月 2020

指纹

探究 'Preparation and characterization of organic-inorganic hybrid ZrOC/PF aerogel used as high-temperature insulator' 的科研主题。它们共同构成独一无二的指纹。

引用此