Low-temperature synthesis and characterization of β-La2S3 nanorods

Kaibin Tang; Changhua An; Pingbo Xie; Guozhen Shen; Yitai Qian

doi:10.1016/S0022-0248(02)01730-X

Low-temperature synthesis and characterization of β-La₂S₃ nanorods

Kaibin Tang^*, Changhua An, Pingbo Xie, Guozhen Shen, Yitai Qian

^*此作品的通讯作者

科研成果: 期刊稿件 › 文章 › 同行评审

18 引用（Scopus）

摘要

β-La₂S₃ nanorods, with diameters of 30-50 nm and lengths of 600-1000 nm, were successfully prepared via a solvothermal route at low temperature. The obtained sample was investigated by means of X-ray powder diffraction, Transmission electronic microscopy and X-ray photoelectronic spectra. The room-temperature photoluminescence spectra of the as-prepared β-La₂S₃ nanorods show a wide emission band peaking at about 420 nm. The possible mechanism for the formation of β-La₂S₃ nanorods was proposed.

源语言	英语
页（从-至）	304-308
页数	5
期刊	Journal of Crystal Growth
卷	245
期	3-4
DOI	https://doi.org/10.1016/S0022-0248(02)01730-X
出版状态	已出版 - 11月 2002
已对外发布	是

访问文件

10.1016/S0022-0248(02)01730-X

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{0d0641d60a7f41b2a2df64e6715a772a,

title = "Low-temperature synthesis and characterization of β-La2S3 nanorods",

abstract = "β-La2S3 nanorods, with diameters of 30-50 nm and lengths of 600-1000 nm, were successfully prepared via a solvothermal route at low temperature. The obtained sample was investigated by means of X-ray powder diffraction, Transmission electronic microscopy and X-ray photoelectronic spectra. The room-temperature photoluminescence spectra of the as-prepared β-La2S3 nanorods show a wide emission band peaking at about 420 nm. The possible mechanism for the formation of β-La2S3 nanorods was proposed.",

keywords = "A1. Nanostructures, A1. X-ray diffraction, B1. Inorganic compounds",

author = "Kaibin Tang and Changhua An and Pingbo Xie and Guozhen Shen and Yitai Qian",

year = "2002",

month = nov,

doi = "10.1016/S0022-0248(02)01730-X",

language = "English",

volume = "245",

pages = "304--308",

journal = "Journal of Crystal Growth",

issn = "0022-0248",

publisher = "Elsevier B.V.",

number = "3-4",

}

TY - JOUR

T1 - Low-temperature synthesis and characterization of β-La2S3 nanorods

AU - Tang, Kaibin

AU - An, Changhua

AU - Xie, Pingbo

AU - Shen, Guozhen

AU - Qian, Yitai

PY - 2002/11

Y1 - 2002/11

N2 - β-La2S3 nanorods, with diameters of 30-50 nm and lengths of 600-1000 nm, were successfully prepared via a solvothermal route at low temperature. The obtained sample was investigated by means of X-ray powder diffraction, Transmission electronic microscopy and X-ray photoelectronic spectra. The room-temperature photoluminescence spectra of the as-prepared β-La2S3 nanorods show a wide emission band peaking at about 420 nm. The possible mechanism for the formation of β-La2S3 nanorods was proposed.

AB - β-La2S3 nanorods, with diameters of 30-50 nm and lengths of 600-1000 nm, were successfully prepared via a solvothermal route at low temperature. The obtained sample was investigated by means of X-ray powder diffraction, Transmission electronic microscopy and X-ray photoelectronic spectra. The room-temperature photoluminescence spectra of the as-prepared β-La2S3 nanorods show a wide emission band peaking at about 420 nm. The possible mechanism for the formation of β-La2S3 nanorods was proposed.

KW - A1. Nanostructures

KW - A1. X-ray diffraction

KW - B1. Inorganic compounds

UR - http://www.scopus.com/inward/record.url?scp=0036852024&partnerID=8YFLogxK

U2 - 10.1016/S0022-0248(02)01730-X

DO - 10.1016/S0022-0248(02)01730-X

M3 - Article

AN - SCOPUS:0036852024

SN - 0022-0248

VL - 245

SP - 304

EP - 308

JO - Journal of Crystal Growth

JF - Journal of Crystal Growth

IS - 3-4

ER -

Low-temperature synthesis and characterization of β-La2S3 nanorods

摘要

访问文件

其它文件与链接

指纹

引用此

Low-temperature synthesis and characterization of β-La₂S₃ nanorods