In-situ preparation of purple-emitting CdS quantum dots using inner PAMAM dendrimer templates

Ri Min Cong; Yun Jun Luo; Guo Ping Li; Hui Min Tan

In-situ preparation of purple-emitting CdS quantum dots using inner PAMAM dendrimer templates

Ri Min Cong^*, Yun Jun Luo, Guo Ping Li, Hui Min Tan

^*此作品的通讯作者

材料学院

Beijing Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

6 引用（Scopus）

摘要

Well-dispersed CdS quantum dots (QDs) with narrow size-distribution were prepared using generation 4.5 ester-terminated PAMAM dendrimers as inner-templates. The average diameter of CdS QDs was 1.5 nm and the photoluminescence was purple. The room temperature photoluminescence quantum yield (RT-PQY) was 0.015. The diameter of CdS QDs increased with the increase of n_Cd2+ / n_PAMAM, also the color of photoluminescence was tunable and could be changed from purple to blue.

源语言	英语
页（从-至）	1763-1766
页数	4
期刊	Chinese Journal of Inorganic Chemistry
卷	21
期	11
出版状态	已出版 - 11月 2005

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{4df009ca37844839a201ba97a4d92e04,

title = "In-situ preparation of purple-emitting CdS quantum dots using inner PAMAM dendrimer templates",

abstract = "Well-dispersed CdS quantum dots (QDs) with narrow size-distribution were prepared using generation 4.5 ester-terminated PAMAM dendrimers as inner-templates. The average diameter of CdS QDs was 1.5 nm and the photoluminescence was purple. The room temperature photoluminescence quantum yield (RT-PQY) was 0.015. The diameter of CdS QDs increased with the increase of nCd2+ / nPAMAM, also the color of photoluminescence was tunable and could be changed from purple to blue.",

keywords = "CdS quantum dots, PAMAM dendrimer, Photoluminescence quantum yield, Tunable photoluminescence",

author = "Cong, {Ri Min} and Luo, {Yun Jun} and Li, {Guo Ping} and Tan, {Hui Min}",

year = "2005",

month = nov,

language = "English",

volume = "21",

pages = "1763--1766",

journal = "Chinese Journal of Inorganic Chemistry",

issn = "1001-4861",

publisher = "Chinese Chemical Society",

number = "11",

}

TY - JOUR

T1 - In-situ preparation of purple-emitting CdS quantum dots using inner PAMAM dendrimer templates

AU - Cong, Ri Min

AU - Luo, Yun Jun

AU - Li, Guo Ping

AU - Tan, Hui Min

PY - 2005/11

Y1 - 2005/11

N2 - Well-dispersed CdS quantum dots (QDs) with narrow size-distribution were prepared using generation 4.5 ester-terminated PAMAM dendrimers as inner-templates. The average diameter of CdS QDs was 1.5 nm and the photoluminescence was purple. The room temperature photoluminescence quantum yield (RT-PQY) was 0.015. The diameter of CdS QDs increased with the increase of nCd2+ / nPAMAM, also the color of photoluminescence was tunable and could be changed from purple to blue.

AB - Well-dispersed CdS quantum dots (QDs) with narrow size-distribution were prepared using generation 4.5 ester-terminated PAMAM dendrimers as inner-templates. The average diameter of CdS QDs was 1.5 nm and the photoluminescence was purple. The room temperature photoluminescence quantum yield (RT-PQY) was 0.015. The diameter of CdS QDs increased with the increase of nCd2+ / nPAMAM, also the color of photoluminescence was tunable and could be changed from purple to blue.

KW - CdS quantum dots

KW - PAMAM dendrimer

KW - Photoluminescence quantum yield

KW - Tunable photoluminescence

UR - http://www.scopus.com/inward/record.url?scp=27744553286&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:27744553286

SN - 1001-4861

VL - 21

SP - 1763

EP - 1766

JO - Chinese Journal of Inorganic Chemistry

JF - Chinese Journal of Inorganic Chemistry

IS - 11

ER -

In-situ preparation of purple-emitting CdS quantum dots using inner PAMAM dendrimer templates

摘要

其它文件与链接

指纹

引用此