Improvement in the oxidation resistance of Nb-Si based alloy by selective laser melting

Yueling Guo; Lina Jia; Bin Kong; Fengxiang Zhang; Jinhui Liu; Hu Zhang

doi:10.1016/j.corsci.2017.08.022

Improvement in the oxidation resistance of Nb-Si based alloy by selective laser melting

Yueling Guo, Lina Jia^*, Bin Kong, Fengxiang Zhang, Jinhui Liu, Hu Zhang

^*此作品的通讯作者

科研成果: 期刊稿件 › 文章 › 同行评审

59 引用（Scopus）

摘要

Nb-18Si-24Ti-2Cr-2Al-2Hf (at.%) alloy was fabricated by selective laser melting (SLM). Results showed that an ultra-fined microstructure was achieved by SLM. After oxidation at 1250 °C for 50 h, the weight gains of Nb-Si based alloys via SLM and vacuum induction melting (VIM) were 96.48 mg/cm² and 198.91 mg/cm², respectively. Compared with the VIM alloy, the SLM alloy exhibited a slower oxidation kinetic rate, featured by the formation of a more compact oxide scale without spallation. The improvement in the oxidation resistance was attributed to the microstructure refinement.

源语言	英语
页（从-至）	260-269
页数	10
期刊	Corrosion Science
卷	127
DOI	https://doi.org/10.1016/j.corsci.2017.08.022
出版状态	已出版 - 10月 2017
已对外发布	是

访问文件

10.1016/j.corsci.2017.08.022

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{75e0862c66bc4078834dcbab6918a000,

title = "Improvement in the oxidation resistance of Nb-Si based alloy by selective laser melting",

abstract = "Nb-18Si-24Ti-2Cr-2Al-2Hf (at.%) alloy was fabricated by selective laser melting (SLM). Results showed that an ultra-fined microstructure was achieved by SLM. After oxidation at 1250 °C for 50 h, the weight gains of Nb-Si based alloys via SLM and vacuum induction melting (VIM) were 96.48 mg/cm2 and 198.91 mg/cm2, respectively. Compared with the VIM alloy, the SLM alloy exhibited a slower oxidation kinetic rate, featured by the formation of a more compact oxide scale without spallation. The improvement in the oxidation resistance was attributed to the microstructure refinement.",

keywords = "Intermetallics, Nb-Si alloy, Oxidation, Rapid solidification, Selective laser melting",

author = "Yueling Guo and Lina Jia and Bin Kong and Fengxiang Zhang and Jinhui Liu and Hu Zhang",

note = "Publisher Copyright: {\textcopyright} 2017 Elsevier Ltd",

year = "2017",

month = oct,

doi = "10.1016/j.corsci.2017.08.022",

language = "English",

volume = "127",

pages = "260--269",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd.",

}

TY - JOUR

T1 - Improvement in the oxidation resistance of Nb-Si based alloy by selective laser melting

AU - Guo, Yueling

AU - Jia, Lina

AU - Kong, Bin

AU - Zhang, Fengxiang

AU - Liu, Jinhui

AU - Zhang, Hu

PY - 2017/10

Y1 - 2017/10

N2 - Nb-18Si-24Ti-2Cr-2Al-2Hf (at.%) alloy was fabricated by selective laser melting (SLM). Results showed that an ultra-fined microstructure was achieved by SLM. After oxidation at 1250 °C for 50 h, the weight gains of Nb-Si based alloys via SLM and vacuum induction melting (VIM) were 96.48 mg/cm2 and 198.91 mg/cm2, respectively. Compared with the VIM alloy, the SLM alloy exhibited a slower oxidation kinetic rate, featured by the formation of a more compact oxide scale without spallation. The improvement in the oxidation resistance was attributed to the microstructure refinement.

AB - Nb-18Si-24Ti-2Cr-2Al-2Hf (at.%) alloy was fabricated by selective laser melting (SLM). Results showed that an ultra-fined microstructure was achieved by SLM. After oxidation at 1250 °C for 50 h, the weight gains of Nb-Si based alloys via SLM and vacuum induction melting (VIM) were 96.48 mg/cm2 and 198.91 mg/cm2, respectively. Compared with the VIM alloy, the SLM alloy exhibited a slower oxidation kinetic rate, featured by the formation of a more compact oxide scale without spallation. The improvement in the oxidation resistance was attributed to the microstructure refinement.

KW - Intermetallics

KW - Nb-Si alloy

KW - Oxidation

KW - Rapid solidification

KW - Selective laser melting

UR - http://www.scopus.com/inward/record.url?scp=85028575489&partnerID=8YFLogxK

U2 - 10.1016/j.corsci.2017.08.022

DO - 10.1016/j.corsci.2017.08.022

M3 - Article

AN - SCOPUS:85028575489

SN - 0010-938X

VL - 127

SP - 260

EP - 269

JO - Corrosion Science

JF - Corrosion Science

ER -

Improvement in the oxidation resistance of Nb-Si based alloy by selective laser melting

摘要

访问文件

其它文件与链接

指纹

引用此