Hydrothermal synthesis and characterization of CuIn2.0Se 3.5 nanocrystallites

Ying Jin; Changhua An; Kaibin Tang; Liying Huang; Guozheng Shen

doi:10.1016/S0167-577X(03)00301-X

Hydrothermal synthesis and characterization of CuIn_2.0Se _3.5 nanocrystallites

Ying Jin, Changhua An, Kaibin Tang^*, Liying Huang, Guozheng Shen

^*此作品的通讯作者

University of Science and Technology of China

科研成果: 期刊稿件 › 文章 › 同行评审

9 引用（Scopus）

摘要

Nanocrystalline CuIn_2.0Se_3.5 was successfully synthesized via a convenient hydrothermal route at relatively low temperature. By changing the selenium sources, the shape of the products can be effectively controlled. The as-prepared products were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum. X-ray photoelectron spectroscopy (XPS) analysis proved the product was ternary compound without secondary phase in it. The factors influencing the formation of the CuIn_2.0Se_3.5 were investigated.

源语言	英语
页（从-至）	4267-4270
页数	4
期刊	Materials Letters
卷	57
期	26-27
DOI	https://doi.org/10.1016/S0167-577X(03)00301-X
出版状态	已出版 - 9月 2003
已对外发布	是

访问文件

10.1016/S0167-577X(03)00301-X

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{7ebb4df61fb54b979fb1f273013494ab,

title = "Hydrothermal synthesis and characterization of CuIn2.0Se 3.5 nanocrystallites",

abstract = "Nanocrystalline CuIn2.0Se3.5 was successfully synthesized via a convenient hydrothermal route at relatively low temperature. By changing the selenium sources, the shape of the products can be effectively controlled. The as-prepared products were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum. X-ray photoelectron spectroscopy (XPS) analysis proved the product was ternary compound without secondary phase in it. The factors influencing the formation of the CuIn2.0Se3.5 were investigated.",

keywords = "CuInSe, Hydrothermal synthesis, Ternary compound",

author = "Ying Jin and Changhua An and Kaibin Tang and Liying Huang and Guozheng Shen",

year = "2003",

month = sep,

doi = "10.1016/S0167-577X(03)00301-X",

language = "English",

volume = "57",

pages = "4267--4270",

journal = "Materials Letters",

issn = "0167-577X",

publisher = "Elsevier B.V.",

number = "26-27",

}

TY - JOUR

T1 - Hydrothermal synthesis and characterization of CuIn2.0Se 3.5 nanocrystallites

AU - Jin, Ying

AU - An, Changhua

AU - Tang, Kaibin

AU - Huang, Liying

AU - Shen, Guozheng

PY - 2003/9

Y1 - 2003/9

N2 - Nanocrystalline CuIn2.0Se3.5 was successfully synthesized via a convenient hydrothermal route at relatively low temperature. By changing the selenium sources, the shape of the products can be effectively controlled. The as-prepared products were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum. X-ray photoelectron spectroscopy (XPS) analysis proved the product was ternary compound without secondary phase in it. The factors influencing the formation of the CuIn2.0Se3.5 were investigated.

AB - Nanocrystalline CuIn2.0Se3.5 was successfully synthesized via a convenient hydrothermal route at relatively low temperature. By changing the selenium sources, the shape of the products can be effectively controlled. The as-prepared products were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum. X-ray photoelectron spectroscopy (XPS) analysis proved the product was ternary compound without secondary phase in it. The factors influencing the formation of the CuIn2.0Se3.5 were investigated.

KW - CuInSe

KW - Hydrothermal synthesis

KW - Ternary compound

UR - http://www.scopus.com/inward/record.url?scp=0042229098&partnerID=8YFLogxK

U2 - 10.1016/S0167-577X(03)00301-X

DO - 10.1016/S0167-577X(03)00301-X

M3 - Article

AN - SCOPUS:0042229098

SN - 0167-577X

VL - 57

SP - 4267

EP - 4270

JO - Materials Letters

JF - Materials Letters

IS - 26-27

ER -

Hydrothermal synthesis and characterization of CuIn2.0Se 3.5 nanocrystallites

摘要

访问文件

其它文件与链接

指纹

引用此

Hydrothermal synthesis and characterization of CuIn_2.0Se _3.5 nanocrystallites