Dynamic ShearProperty and Failure Analysis of 603 Steel

Zhong Yue Sun; Ze Jian Xu; Yu Liu; Yi Tong; Feng Lei Huang

Dynamic ShearProperty and Failure Analysis of 603 Steel

Zhong Yue Sun, Ze Jian Xu^*, Yu Liu, Yi Tong, Feng Lei Huang

^*此作品的通讯作者

机电学院

Beijing Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

Dynamic shear properties of 603 steel were tested by the new Hopkinson bar loading technology, and the microscopic failure mechanism was analyzed. The shear stress-shear strain curves of the material were obtained at strain rates above 10⁴ s^-1, and failure parameters of the material were determined. The results show that with the increase of strain rate, the flow stress shows an obvious strengthening effect, while the failure stress increases slightly, and the failure strain decreases gradually. With ABAQUS/Explicit finite element analysis, the calculated shear stress-shear strain curves agree well with the experimental results. Fracture analysis shows that the failure mode of the material is ductile fracture, and it is influenced by adiabatic shear bands. With the increase of strain rate, the effect of adiabatic shear band is more obvious.

源语言	英语
页（从-至）	137-141
页数	5
期刊	Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology
卷	37
出版状态	已出版 - 1 12月 2017

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{ccfeee63f25447e6b5e877641a61d768,

title = "Dynamic ShearProperty and Failure Analysis of 603 Steel",

abstract = "Dynamic shear properties of 603 steel were tested by the new Hopkinson bar loading technology, and the microscopic failure mechanism was analyzed. The shear stress-shear strain curves of the material were obtained at strain rates above 104 s-1, and failure parameters of the material were determined. The results show that with the increase of strain rate, the flow stress shows an obvious strengthening effect, while the failure stress increases slightly, and the failure strain decreases gradually. With ABAQUS/Explicit finite element analysis, the calculated shear stress-shear strain curves agree well with the experimental results. Fracture analysis shows that the failure mode of the material is ductile fracture, and it is influenced by adiabatic shear bands. With the increase of strain rate, the effect of adiabatic shear band is more obvious.",

keywords = "Dynamic shear, Fracture analysis, High strain rate, Numerical simulation",

author = "Sun, {Zhong Yue} and Xu, {Ze Jian} and Yu Liu and Yi Tong and Huang, {Feng Lei}",

year = "2017",

month = dec,

day = "1",

language = "English",

volume = "37",

pages = "137--141",

journal = "Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology",

issn = "1001-0645",

publisher = "Beijing Institute of Technology",

}

TY - JOUR

T1 - Dynamic ShearProperty and Failure Analysis of 603 Steel

AU - Sun, Zhong Yue

AU - Xu, Ze Jian

AU - Liu, Yu

AU - Tong, Yi

AU - Huang, Feng Lei

PY - 2017/12/1

Y1 - 2017/12/1

N2 - Dynamic shear properties of 603 steel were tested by the new Hopkinson bar loading technology, and the microscopic failure mechanism was analyzed. The shear stress-shear strain curves of the material were obtained at strain rates above 104 s-1, and failure parameters of the material were determined. The results show that with the increase of strain rate, the flow stress shows an obvious strengthening effect, while the failure stress increases slightly, and the failure strain decreases gradually. With ABAQUS/Explicit finite element analysis, the calculated shear stress-shear strain curves agree well with the experimental results. Fracture analysis shows that the failure mode of the material is ductile fracture, and it is influenced by adiabatic shear bands. With the increase of strain rate, the effect of adiabatic shear band is more obvious.

AB - Dynamic shear properties of 603 steel were tested by the new Hopkinson bar loading technology, and the microscopic failure mechanism was analyzed. The shear stress-shear strain curves of the material were obtained at strain rates above 104 s-1, and failure parameters of the material were determined. The results show that with the increase of strain rate, the flow stress shows an obvious strengthening effect, while the failure stress increases slightly, and the failure strain decreases gradually. With ABAQUS/Explicit finite element analysis, the calculated shear stress-shear strain curves agree well with the experimental results. Fracture analysis shows that the failure mode of the material is ductile fracture, and it is influenced by adiabatic shear bands. With the increase of strain rate, the effect of adiabatic shear band is more obvious.

KW - Dynamic shear

KW - Fracture analysis

KW - High strain rate

KW - Numerical simulation

UR - http://www.scopus.com/inward/record.url?scp=85047191660&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:85047191660

SN - 1001-0645

VL - 37

SP - 137

EP - 141

JO - Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology

JF - Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology

ER -

Dynamic ShearProperty and Failure Analysis of 603 Steel

摘要

其它文件与链接

指纹

引用此