Effect of rare earth lanthanum-cerium doping on corrosion behavior of zinc-aluminum-magnesium hot-dip galvanizing coatings used for transmission towers

Purpose: The purpose of this study is to improve the corrosion resistance of the transmission towers by Zinc-aluminum-magnesium (Zn-Al-Mg) coatings doped with rare earths lanthanum (La) and cerium (Ce) (denoted as Zn-Al-Mg-Re) in Q345 steel. Design/methodology/approach: The phase structure of Zn-Al-Mg-Re composite coatings has been determined by X-ray diffraction, whereas their surface morphology and cross-sectional microstructure as well as cross-sectional elemental composition have been analyzed by scanning electron microscopy and energy-dispersive spectrometry. Moreover, the corrosion resistance of Zn-Al-Mg-Re composite coatings has been evaluated by acetic acid accelerated salt spray test of copper strip. Findings: Experimental results show that doping with La and Ce favors to tune the composition (along with the generation of new phase, such as LaAl₃ or Al₁₁Ce₃) and refine the microstructure of Zn-Al-Mg galvanizing coatings, thereby significantly improving the corrosion resistance of the coatings. Particularly, Zn-Al-Mg-Re with 0.15% (mass fraction) La exhibits the best corrosion resistance among the tested galvanizing coatings. Originality/Value: Zinc-aluminum-magnesium (Zn-Al-Mg) coatings doped with rare earths lanthanum (La) and cerium (Ce) (denoted as Zn-Al-Mg-Re) have been prepared on Q345 steel substrate by hot-dip galvanizing so as to improve the corrosion resistance of the transmission towers, and to understand the corrosion inhibition of the Zn-Al-Mg-Re coating.