Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K0.2Mn1.4Cr(CN) 6·6H2O

Zhengliang Lu; Xinyi Wang; Zhiliang Liu; Fuhui Liao; Song Gao; Rengen Xiong; Hongwei Ma; Deqing Zhang; Daoben Zhu

doi:10.1021/ic051145f

Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K_0.2Mn_1.4Cr(CN) ₆·6H₂O

Zhengliang Lu, Xinyi Wang, Zhiliang Liu, Fuhui Liao, Song Gao^*, Rengen Xiong, Hongwei Ma, Deqing Zhang, Daoben Zhu

^*此作品的通讯作者

科研成果: 期刊稿件 › 文章 › 同行评审

74 引用（Scopus）

摘要

A new complex (1) of Prussian blue analogue with the composition of K _0.2Mn_1.4Cr(CN)₆·6H₂O was prepared and characterized structurally as well as magnetically. The crystal structure of complex 1 was determined by X-ray diffraction analysis. The results indicate that complex 1 consists of a 3D cubic lattice similar to those of Mn₃[Cr(CN)₆]₂·χH₂O, Mn₃[Co(CN)₆]₂·χH₂O, Cd₃[Cr(CN)₆]₂·χH₂O, and Cd₃[Co(CN)₆]₂·chi;H₂O. Magnetic measurements show that complex 1 is a ferrimagnet with T_c = 66 K. It is interesting to note that the magnetic behavior of complex 1 can be substantially modulated through a dehydration/rehydration treatment. The T _c value of this ferrimagnet increases to 99 K after dehydration reaching a 23.4% weight loss, and it decreases back to 66 K after the dehydrated sample reabsorbs water molecules.

源语言	英语
页（从-至）	999-1004
页数	6
期刊	Inorganic Chemistry
卷	45
期	3
DOI	https://doi.org/10.1021/ic051145f
出版状态	已出版 - 6 2月 2006
已对外发布	是

访问文件

10.1021/ic051145f

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{ab130cb63e3749ae91e954af3ca62c5e,

title = "Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K0.2Mn1.4Cr(CN) 6·6H2O",

abstract = "A new complex (1) of Prussian blue analogue with the composition of K 0.2Mn1.4Cr(CN)6·6H2O was prepared and characterized structurally as well as magnetically. The crystal structure of complex 1 was determined by X-ray diffraction analysis. The results indicate that complex 1 consists of a 3D cubic lattice similar to those of Mn3[Cr(CN)6]2·χH2O, Mn3[Co(CN)6]2·χH2O, Cd3[Cr(CN)6]2·χH2O, and Cd3[Co(CN)6]2·chi;H2O. Magnetic measurements show that complex 1 is a ferrimagnet with Tc = 66 K. It is interesting to note that the magnetic behavior of complex 1 can be substantially modulated through a dehydration/rehydration treatment. The T c value of this ferrimagnet increases to 99 K after dehydration reaching a 23.4% weight loss, and it decreases back to 66 K after the dehydrated sample reabsorbs water molecules.",

author = "Zhengliang Lu and Xinyi Wang and Zhiliang Liu and Fuhui Liao and Song Gao and Rengen Xiong and Hongwei Ma and Deqing Zhang and Daoben Zhu",

year = "2006",

month = feb,

day = "6",

doi = "10.1021/ic051145f",

language = "English",

volume = "45",

pages = "999--1004",

journal = "Inorganic Chemistry",

issn = "0020-1669",

publisher = "American Chemical Society",

number = "3",

}

TY - JOUR

T1 - Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K0.2Mn1.4Cr(CN) 6·6H2O

AU - Lu, Zhengliang

AU - Wang, Xinyi

AU - Liu, Zhiliang

AU - Liao, Fuhui

AU - Gao, Song

AU - Xiong, Rengen

AU - Ma, Hongwei

AU - Zhang, Deqing

AU - Zhu, Daoben

PY - 2006/2/6

Y1 - 2006/2/6

N2 - A new complex (1) of Prussian blue analogue with the composition of K 0.2Mn1.4Cr(CN)6·6H2O was prepared and characterized structurally as well as magnetically. The crystal structure of complex 1 was determined by X-ray diffraction analysis. The results indicate that complex 1 consists of a 3D cubic lattice similar to those of Mn3[Cr(CN)6]2·χH2O, Mn3[Co(CN)6]2·χH2O, Cd3[Cr(CN)6]2·χH2O, and Cd3[Co(CN)6]2·chi;H2O. Magnetic measurements show that complex 1 is a ferrimagnet with Tc = 66 K. It is interesting to note that the magnetic behavior of complex 1 can be substantially modulated through a dehydration/rehydration treatment. The T c value of this ferrimagnet increases to 99 K after dehydration reaching a 23.4% weight loss, and it decreases back to 66 K after the dehydrated sample reabsorbs water molecules.

AB - A new complex (1) of Prussian blue analogue with the composition of K 0.2Mn1.4Cr(CN)6·6H2O was prepared and characterized structurally as well as magnetically. The crystal structure of complex 1 was determined by X-ray diffraction analysis. The results indicate that complex 1 consists of a 3D cubic lattice similar to those of Mn3[Cr(CN)6]2·χH2O, Mn3[Co(CN)6]2·χH2O, Cd3[Cr(CN)6]2·χH2O, and Cd3[Co(CN)6]2·chi;H2O. Magnetic measurements show that complex 1 is a ferrimagnet with Tc = 66 K. It is interesting to note that the magnetic behavior of complex 1 can be substantially modulated through a dehydration/rehydration treatment. The T c value of this ferrimagnet increases to 99 K after dehydration reaching a 23.4% weight loss, and it decreases back to 66 K after the dehydrated sample reabsorbs water molecules.

UR - http://www.scopus.com/inward/record.url?scp=32644434329&partnerID=8YFLogxK

U2 - 10.1021/ic051145f

DO - 10.1021/ic051145f

M3 - Article

AN - SCOPUS:32644434329

SN - 0020-1669

VL - 45

SP - 999

EP - 1004

JO - Inorganic Chemistry

JF - Inorganic Chemistry

IS - 3

ER -

Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K0.2Mn1.4Cr(CN) 6·6H2O

摘要

访问文件

其它文件与链接

指纹

引用此

Tuning the magnetic behavior via dehydration/hydration treatment of a new ferrimagnet with the composition of K_0.2Mn_1.4Cr(CN) ₆·6H₂O