T1 - Synthesis of Al2O3-Y2O3 Ceramic Coatings on the Fe-Cr-Al Wire via Aqueous Cathodic Plasma Electrolysis
AU - Zhang, Yuping
AU - Chen, Chao
AU - Chen, Weiwei
AU - Cheng, Huanwu
AU - Wang, Yingchun
AU - Wang, Lu
N1 - Publisher Copyright:
© 2017 American Chemical Society.
PY - 2017/12/27
Y1 - 2017/12/27
N2 - The Al2O3-Y2O3 coating was successfully prepared by cathodic plasma electrolysis on the FeCrAl wire. Influences of the electrolyte composition and the processing parameters on the microstructure and property of the Al2O3-Y2O3 ceramic coating were systematically investigated. The coating was mainly composed of γ-Al2O3, α-Al2O3, and Y2O3. Experimental results showed that the thickness of the coating was gradually increased with the increase of working voltage, while the bonding became poor. With an increase in the deposition time, the thickness and the electrical resistance of the Al2O3-Y2O3 coating were increased in a certain range. When the Al2O3-Y2O3 coating was deposited at 110 V for 60-90 s, the bonding between the coating and the substrate was superior, and the coating microstructure was dense, continuous, and uniform with the electrical resistance reaching up to ∼40 Mω. The formation mechanism of the coating was also discussed based on the electrochemical mechanism and the plasma discharge.
AB - The Al2O3-Y2O3 coating was successfully prepared by cathodic plasma electrolysis on the FeCrAl wire. Influences of the electrolyte composition and the processing parameters on the microstructure and property of the Al2O3-Y2O3 ceramic coating were systematically investigated. The coating was mainly composed of γ-Al2O3, α-Al2O3, and Y2O3. Experimental results showed that the thickness of the coating was gradually increased with the increase of working voltage, while the bonding became poor. With an increase in the deposition time, the thickness and the electrical resistance of the Al2O3-Y2O3 coating were increased in a certain range. When the Al2O3-Y2O3 coating was deposited at 110 V for 60-90 s, the bonding between the coating and the substrate was superior, and the coating microstructure was dense, continuous, and uniform with the electrical resistance reaching up to ∼40 Mω. The formation mechanism of the coating was also discussed based on the electrochemical mechanism and the plasma discharge.
UR - http://www.scopus.com/inward/record.url?scp=85040193239&partnerID=8YFLogxK
U2 - 10.1021/acs.iecr.7b03661
DO - 10.1021/acs.iecr.7b03661
M3 - Article
AN - SCOPUS:85040193239
SN - 0888-5885
VL - 56
SP - 15058
EP - 15064
JO - Industrial and Engineering Chemistry Research
JF - Industrial and Engineering Chemistry Research
IS - 51
ER -