Study of interface reaction in the Si3N4/Al composite prepared by pressureless infiltration

Yang Wei Wang*, Fu Chi Wang, Xiao Dong Yu, Jun Tao Li

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

4 引用 (Scopus)

摘要

It is significant to study the relationship between the oxidation level of the Si3N4 porous preform and the interface reaction for providing the base of optimizing designation of the Si3N4/Al composite. The preforms with different oxidation level were pressurelessly infiltrated under the same processing conditions. Oxygen content of the preforms, phase constituents, and hardness of the composites were characterized by EDS, XRD instruments and Rockwell hardness tester respectively. The XRD results showed that the Si3N4/Al composite contain Al, Si3N4, A1N and a small amount of Si, Mg2Si, MgO, MgAl2O4. With the increasing oxidation level of preforms, the reaction product of A1N decreased remarkably and MgO increased. More MgAl2O4 were measured from the composite which preform presintered at the higher temperature of 1200°C. The hardness of composite went down with the increasing of the oxidation level of preform. It is an important reason for the reduction of the hardness of composites that the oxide over Si3N4 particles results in the decreasing of replacement reaction between Al-Mg melt and Si3N4.

源语言英语
页(从-至)55-58
页数4
期刊Hangkong Cailiao Xuebao/Journal of Aeronautical Materials
26
1
出版状态已出版 - 2月 2006

指纹

探究 'Study of interface reaction in the Si3N4/Al composite prepared by pressureless infiltration' 的科研主题。它们共同构成独一无二的指纹。

引用此