Studies on the viscoelastic phase separation in epoxy resin modified with polyethersulfone

Xiao Lin Tang; Lin Xia Zhang; Tao Wang; Shan Jun Li

Studies on the viscoelastic phase separation in epoxy resin modified with polyethersulfone

Xiao Lin Tang^*, Lin Xia Zhang, Tao Wang, Shan Jun Li

^*此作品的通讯作者

Fudan University

科研成果: 期刊稿件 › 文章 › 同行评审

5 引用（Scopus）

摘要

The phase separation evolution of polyethersulfone/epoxy resin/4,4′-methylene-bis(2,6-dimethylaniline) blends was investigated by optical microscopy (OM), time resolved light scattering (TRLS) and scanning electron microscopy (SEM). The experimental results indicate that there exists viscoelastic effect on the phase separation evolution. The double phase separation was observed in the blend with lower content of PES (13.2 wt% and 15.9 wt%) cured at 120 and 140 °C. However, this phenomenon did not occur when the higher PES content blend (18.5 wt%) was cured at the same temperatures.

源语言	英语
页（从-至）	321-326
页数	6
期刊	Acta Chimica Sinica
卷	63
期	4
出版状态	已出版 - 2005
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{e82225dd059f44229d2778961216d7e5,

title = "Studies on the viscoelastic phase separation in epoxy resin modified with polyethersulfone",

abstract = "The phase separation evolution of polyethersulfone/epoxy resin/4,4′-methylene-bis(2,6-dimethylaniline) blends was investigated by optical microscopy (OM), time resolved light scattering (TRLS) and scanning electron microscopy (SEM). The experimental results indicate that there exists viscoelastic effect on the phase separation evolution. The double phase separation was observed in the blend with lower content of PES (13.2 wt% and 15.9 wt%) cured at 120 and 140 °C. However, this phenomenon did not occur when the higher PES content blend (18.5 wt%) was cured at the same temperatures.",

keywords = "Double phase separation, Thermoplastic-thermoset blends, Viscoelastic",

author = "Tang, {Xiao Lin} and Zhang, {Lin Xia} and Tao Wang and Li, {Shan Jun}",

year = "2005",

language = "English",

volume = "63",

pages = "321--326",

journal = "Acta Chimica Sinica",

issn = "0567-7351",

publisher = "Science Press",

number = "4",

}

TY - JOUR

T1 - Studies on the viscoelastic phase separation in epoxy resin modified with polyethersulfone

AU - Tang, Xiao Lin

AU - Zhang, Lin Xia

AU - Wang, Tao

AU - Li, Shan Jun

PY - 2005

Y1 - 2005

N2 - The phase separation evolution of polyethersulfone/epoxy resin/4,4′-methylene-bis(2,6-dimethylaniline) blends was investigated by optical microscopy (OM), time resolved light scattering (TRLS) and scanning electron microscopy (SEM). The experimental results indicate that there exists viscoelastic effect on the phase separation evolution. The double phase separation was observed in the blend with lower content of PES (13.2 wt% and 15.9 wt%) cured at 120 and 140 °C. However, this phenomenon did not occur when the higher PES content blend (18.5 wt%) was cured at the same temperatures.

AB - The phase separation evolution of polyethersulfone/epoxy resin/4,4′-methylene-bis(2,6-dimethylaniline) blends was investigated by optical microscopy (OM), time resolved light scattering (TRLS) and scanning electron microscopy (SEM). The experimental results indicate that there exists viscoelastic effect on the phase separation evolution. The double phase separation was observed in the blend with lower content of PES (13.2 wt% and 15.9 wt%) cured at 120 and 140 °C. However, this phenomenon did not occur when the higher PES content blend (18.5 wt%) was cured at the same temperatures.

KW - Double phase separation

KW - Thermoplastic-thermoset blends

KW - Viscoelastic

UR - http://www.scopus.com/inward/record.url?scp=33749152540&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:33749152540

SN - 0567-7351

VL - 63

SP - 321

EP - 326

JO - Acta Chimica Sinica

JF - Acta Chimica Sinica

IS - 4

ER -

Studies on the viscoelastic phase separation in epoxy resin modified with polyethersulfone

摘要

其它文件与链接

指纹

引用此