Ying Yuan, Dongfang Shi, Suo He, Huanguo Guo, Yuanfeng Zheng, Yong Zhang, Haifu Wang*

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

7 引用 (Scopus)

摘要

In recent years, polytetrafluoroethylene (PTFE)/aluminum (Al) energetic materials with high-energy density have attracted extensive attention and have broad application prospects, but the low-energy release efficiency restricts their application. In this paper, oxide, bismuth trioxide (Bi2O3 ) or molybdenum trioxide (MoO3 ) are introduced into PTFE/Al to improve the chemical reaction performance of energetic materials. The pressurization characteristics of PTFE/Al/oxide as pressure generators are compared and analyzed. The experiments show that the significantly optimized quasistatic pressure peak, impulse, and energy release efficiency (0.162 MPa, 10.177 s·kPa, and 0.74) are achieved for PTFE/Al by adding 30 wt.% Bi2O3 . On the other hand, the optimal parameter obtained by adding 10% MoO3 is 0.147 MPa, 9.184 s·kPa, and 0.68. Further, the mechanism of enhancing the energy release performance of PTFE/Al through oxide is revealed. The mechanism analysis shows that the shock-induced energy release performance of PTFE/Al energetic material is affected by the intensity of the shock wave and the chemical reaction extent of the material under the corresponding intensity. The oxide to PTFE/Al increases the intensity of the shock wave in the material, but the chemical reaction extent of the material decreases under the corresponding intensity.

源语言英语
文章编号3042
期刊Materials
15
9
DOI
出版状态已出版 - 1 5月 2022

指纹

探究 'Shock-Induced Energy Release Performances of PTFE/Al/Oxide' 的科研主题。它们共同构成独一无二的指纹。

引用此