T1 - Properties of GAP/PET dual-soft segments energetic polyurethane elastomer
AU - Wang, Xupeng
AU - Luo, Yunjun
AU - Wang, Xiaoqing
AU - Ge, Zhen
PY - 2010/3
Y1 - 2010/3
N2 - To improve the performance of glycidyl azide polymer(GAP), by using trimethylolpropane (TMP) as a crosslinker, isophorone diisocyanate(IPDI) as the curing agent, glycidyl azide polymer/ethylene oxide-tetrahydrofuran copolyether (PET) dual-soft segments energetic polyurethane elastomer was synthesized. The elastomer was characterized with FTIR, DSC, XRD and other means. The experimental results showed that some differences in the reaction rates of PET/IPDI and GAP/IPDI were observed at the content of catalyst was 0.1%, but PET and GAP could participate in the formation of polyurethane elastomer together. When PET was introduced in the elastomer, the tensile strength of elastomer increased by 0.9 MPa, elongation increased by 156%. The Tg of two soft segments were observed and its values changed with the content of two soft segments. GAP/PET/TMP/IPDI elastomer was an amorphous polymer and began to decompose at 183°C.
AB - To improve the performance of glycidyl azide polymer(GAP), by using trimethylolpropane (TMP) as a crosslinker, isophorone diisocyanate(IPDI) as the curing agent, glycidyl azide polymer/ethylene oxide-tetrahydrofuran copolyether (PET) dual-soft segments energetic polyurethane elastomer was synthesized. The elastomer was characterized with FTIR, DSC, XRD and other means. The experimental results showed that some differences in the reaction rates of PET/IPDI and GAP/IPDI were observed at the content of catalyst was 0.1%, but PET and GAP could participate in the formation of polyurethane elastomer together. When PET was introduced in the elastomer, the tensile strength of elastomer increased by 0.9 MPa, elongation increased by 156%. The Tg of two soft segments were observed and its values changed with the content of two soft segments. GAP/PET/TMP/IPDI elastomer was an amorphous polymer and began to decompose at 183°C.
KW - Copolymerization
KW - Glycidyl azide polymer
KW - Modification
KW - Polyurethane
UR - http://www.scopus.com/inward/record.url?scp=77951018645&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:77951018645
SN - 0438-1157
VL - 61
SP - 784
EP - 788
JO - Huagong Xuebao/CIESC Journal
JF - Huagong Xuebao/CIESC Journal
IS - 3
ER -