Preparation and characterization of phenolic aerogels from a new kind of reaction system

Jian Zheng; Zhi Feng Lin; Yun Jun Luo

Preparation and characterization of phenolic aerogels from a new kind of reaction system

Jian Zheng^*, Zhi Feng Lin, Yun Jun Luo

^*此作品的通讯作者

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

1 引用（Scopus）

摘要

Aerogels were prepared via sol-gel polymerization of a new reaction system (5-methylresorcinol- furfural) which was catalyzed by NaOH(C). The relation of progress and aerogel structure was investigated by SEM and Surface Area and Pore Size Analyzer. The results show that mass content of reactants influences the particle siza more greatly. Pore size distribution changes greatly with mass content of reactants and MR/C(molar ratio). The average pore diameter is about 5~20 nm, and the surface aera is about 400~550 g/m², which is more larger than that of resorcinol-furfural aerogel.

源语言	英语
页（从-至）	135-138+143
期刊	Cailiao Kexue yu Gongyi/Material Science and Technology
卷	19
期	5
出版状态	已出版 - 10月 2011

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{1ce37076587d43ebbfd289a726c240ac,

title = "Preparation and characterization of phenolic aerogels from a new kind of reaction system",

abstract = "Aerogels were prepared via sol-gel polymerization of a new reaction system (5-methylresorcinol- furfural) which was catalyzed by NaOH(C). The relation of progress and aerogel structure was investigated by SEM and Surface Area and Pore Size Analyzer. The results show that mass content of reactants influences the particle siza more greatly. Pore size distribution changes greatly with mass content of reactants and MR/C(molar ratio). The average pore diameter is about 5~20 nm, and the surface aera is about 400~550 g/m2, which is more larger than that of resorcinol-furfural aerogel.",

keywords = "5-methylresorcinol, Aerogels, Furfural, Structure",

author = "Jian Zheng and Lin, {Zhi Feng} and Luo, {Yun Jun}",

year = "2011",

month = oct,

language = "English",

volume = "19",

pages = "135--138+143",

journal = "Cailiao Kexue yu Gongyi/Material Science and Technology",

issn = "1005-0299",

publisher = "Harbin Institute of Technology",

number = "5",

}

TY - JOUR

T1 - Preparation and characterization of phenolic aerogels from a new kind of reaction system

AU - Zheng, Jian

AU - Lin, Zhi Feng

AU - Luo, Yun Jun

PY - 2011/10

Y1 - 2011/10

N2 - Aerogels were prepared via sol-gel polymerization of a new reaction system (5-methylresorcinol- furfural) which was catalyzed by NaOH(C). The relation of progress and aerogel structure was investigated by SEM and Surface Area and Pore Size Analyzer. The results show that mass content of reactants influences the particle siza more greatly. Pore size distribution changes greatly with mass content of reactants and MR/C(molar ratio). The average pore diameter is about 5~20 nm, and the surface aera is about 400~550 g/m2, which is more larger than that of resorcinol-furfural aerogel.

AB - Aerogels were prepared via sol-gel polymerization of a new reaction system (5-methylresorcinol- furfural) which was catalyzed by NaOH(C). The relation of progress and aerogel structure was investigated by SEM and Surface Area and Pore Size Analyzer. The results show that mass content of reactants influences the particle siza more greatly. Pore size distribution changes greatly with mass content of reactants and MR/C(molar ratio). The average pore diameter is about 5~20 nm, and the surface aera is about 400~550 g/m2, which is more larger than that of resorcinol-furfural aerogel.

KW - 5-methylresorcinol

KW - Aerogels

KW - Furfural

KW - Structure

UR - http://www.scopus.com/inward/record.url?scp=83055179883&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:83055179883

SN - 1005-0299

VL - 19

SP - 135-138+143

JO - Cailiao Kexue yu Gongyi/Material Science and Technology

JF - Cailiao Kexue yu Gongyi/Material Science and Technology

IS - 5

ER -