Preparation and characterization of Mg-P coatings on Mg-Zn-Y-Nd alloy for corrosion protection

Y. Pan, C. Tan*, J. Han*, G. Liu

*此作品的通讯作者

科研成果: 期刊稿件会议文章同行评审

摘要

To improve the corrosion resistance of Mg-Zn-Y-Nd alloy, Mg-P coatings were prepared on the surface by a simple chemical conversion method. The Mg-P coatings were optimized by regulating the reaction conditions such as the pH value of the conversion solution (4.2, 5, 6, and 7), treatment temperature (20 °C, 40 °C, and 80 °C), and treatment time (1 h, 2 h, and 3 h) in this study. Scanning electron microscopy (SEM) showed that the optimized Mg-P coating has a uniform surface structure. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) results demonstrated that the Mg-P coating consists of MgNH4PO4·6H2O and MgHPO4·3H2O. The cross-sectional morphology revealed that the Mg-P coating has a rough structure with a thickness of 8 μm. The effect of Mg-P coating on the corrosion resistance of Mg-Zn-Y-Nd alloy was investigated by in vitro immersion test, and it was found that the corrosion rate was effectively decelerated within 10 days. In summary, we studied the effects of reaction conditions for preparing Mg-P coatings on the surface of Mg-Zn-Y-Nd alloy by a chemical conversion method and effectively improving the corrosion resistance of Mg-Zn-Y-Nd alloy.

源语言英语
文章编号012033
期刊Journal of Physics: Conference Series
2639
1
DOI
出版状态已出版 - 2023
活动Chinese Materials Conference 2022-2023 - Shenzhen, 中国
期限: 7 7月 202310 7月 2023

指纹

探究 'Preparation and characterization of Mg-P coatings on Mg-Zn-Y-Nd alloy for corrosion protection' 的科研主题。它们共同构成独一无二的指纹。

引用此