Operational test of bonded magnetocaloric plates

Christian R.H. Bahl*, Kristina Navickaitė, Henrique Neves Bez, Tian Lei, Kurt Engelbrecht, Rasmus Bjørk, Ke Li, Zhenxing Li, Jun Shen, Wei Dai, Jichen Jia, Yuanyuan Wu, Yi Long, Fengxia Hu, Baogen Shen

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

24 引用 (Scopus)

摘要

Bonded plates made by hot pressing La0.85Ce0.15Fe11.25Mn0.25Si1.5Hy particles and resin have been tested as active magnetic regenerators in a small scale magnetocaloric device. Firstly, the plates were carefully characterised magnetically and thermally. The plates were prepared with 5 wt% resin, and from density measurements it was found that the volume ratio of the magnetocaloric material in the plates was 0.53, due to the resin and porosity. The best operating conditions for the plate regenerator were determined at which a temperature span of 6.4 K was measured along the plates.

源语言英语
页(从-至)245-251
页数7
期刊International Journal of Refrigeration
76
DOI
出版状态已出版 - 1 4月 2017
已对外发布

指纹

探究 'Operational test of bonded magnetocaloric plates' 的科研主题。它们共同构成独一无二的指纹。

引用此