Novel flame retardancy effects of DOPO-POSS on epoxy resins

A series of flame retarded epoxy resins (EP) was prepared with a novel polyhedral oligomeric silsesquioxane containing 9,10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide (DOPO-POSS). The flame retardancy of these EPs was tested by the LOI, UL-94, which indicates that DOPO-POSS has meaningful effects on the flame retardancy of EP composites. 2.5 wt.% DOPO-POSS incorporation into epoxy resin (EP-2.5), results in a LOI value 30.2 and UL-94 V-1 (t₁ = 8 s and t₂ = 3 s) rating. Moreover, self-extinguishing effect through the pyrolytic gases spurt is observed in UL-94 test for the EP-2.5. The pyrolytic gases and thermal stability of epoxy resins with and without DOPO-POSS were detected by TGA-FTIR under air atmosphere. Releases of gaseous species are found to be similar for the pure EP and EP-2.5. The details of fire behaviour, such as TTI, HRR, p-HRR, TSR, SEA, COPR, CO₂PR, and TML, were tested by cone calorimeter. It is notable that 2.5 wt.% DOPO-POSS could make COPR and CO₂PR reach a maximum, which could explain the blowing-out extinguishing effect.