Mo2Ti2C3 and PTFE synergistically functionalized corrosion-resistant, thermally conductive, super abrasion-resistant epoxy resin composite coating

Guojing Chen, Yixi Xu, Zhenqian Ma, Xinrui Wang, Chunpeng Chai*

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

5 引用 (Scopus)

摘要

Epoxy resin (EP) matrix composites are a widely used polymer-based protective coating material. However, the low lubricity leads to frictional wear problems that make their large-scale development and application a serious challenge. Based on this, a multifunctional composite coating (MPT-EP) with low wear, high lubricity, high thermal conductivity, and corrosion resistance was prepared by introducing polytetrafluoroethylene (PTFE) and lamellar Mo2Ti2C3 as a composite lubricant into epoxy resin matrix using a simple solvent dispersion method. The results showed that the introduction of the composite lubricant resulted in enhanced hardness and mechanical properties of the composite coating. Compared with the single epoxy resin coating (0.31), the friction coefficient (COF) of the composite coating was only 0.22, and the friction surface did not show obvious abrasion marks. The surface temperature of the composite coating was up to 51.4 °C when it was placed on a hot bench at 60 °C for 60 s. In addition, the COF of the composite coating did not change significantly after being immersed in acid, alkali and salt solutions. Therefore, the Mo2Ti2C3-induced multifunctional epoxy resin matrix composites have important application potential and research value in the field of ultra-wear-resistant and high lubrication protective coatings.

源语言英语
文章编号131090
期刊Surface and Coatings Technology
489
DOI
出版状态已出版 - 15 8月 2024

指纹

探究 'Mo2Ti2C3 and PTFE synergistically functionalized corrosion-resistant, thermally conductive, super abrasion-resistant epoxy resin composite coating' 的科研主题。它们共同构成独一无二的指纹。

引用此

Chen, G., Xu, Y., Ma, Z., Wang, X., & Chai, C. (2024). Mo2Ti2C3 and PTFE synergistically functionalized corrosion-resistant, thermally conductive, super abrasion-resistant epoxy resin composite coating. Surface and Coatings Technology, 489, 文章 131090. https://doi.org/10.1016/j.surfcoat.2024.131090