Morphology character and thermal behavior of CNTs/KClO4

Bu Yun Zhang; Qing Jie Jiao; Hui Ren; Yong Jie Jia; Kuo Zhang; Guan Nan Wu; Guo Quan Liu

doi:10.3969/j.issn.1006-9941.2011.04.011

Morphology character and thermal behavior of CNTs/KClO₄

Bu Yun Zhang^*, Qing Jie Jiao, Hui Ren, Yong Jie Jia, Kuo Zhang, Guan Nan Wu, Guo Quan Liu

^*此作品的通讯作者

机电学院

科研成果: 期刊稿件 › 文章 › 同行评审

6 引用（Scopus）

摘要

The carbon nano-tubes/potassium perchlorate (CNTs/KClO₄) composite was prepared via a double decomposition reaction of NH₄ClO₄ solution and KOH solution in the presence of carbon nano-tubes. Morphology character and thermal behavior of the composite were studied by scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimeter (DSC) and specific surface area (SSA) analyses. Results show that KClO₄ prepared by this method is coated on the surface of CNTs effectively. In comparion with pure CNTs, the diameter of CNTs supporting KClO₄ increases significantly and the SSA of the CNTs/KClO₄ composite decreases by 40.719 m²·g^-1. In comparion with KClO₄, the thermal decomposition temperature of the composite decreases by 75°C and crystal transformation peak temperature decrease by 5°C. In comparion with Mo/KClO₄, the thermal conductivity of Mo/KClO₄ ignition composition prepared by CNTs/KClO₄ increases by 33.9%.

源语言	英语
页（从-至）	401-404
页数	4
期刊	Hanneng Cailiao/Chinese Journal of Energetic Materials
卷	19
期	4
DOI	https://doi.org/10.3969/j.issn.1006-9941.2011.04.011
出版状态	已出版 - 8月 2011

访问文件

10.3969/j.issn.1006-9941.2011.04.011

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{1b14fadc526d467d9c9b78eb8e9533e2,

title = "Morphology character and thermal behavior of CNTs/KClO4",

abstract = "The carbon nano-tubes/potassium perchlorate (CNTs/KClO4) composite was prepared via a double decomposition reaction of NH4ClO4 solution and KOH solution in the presence of carbon nano-tubes. Morphology character and thermal behavior of the composite were studied by scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimeter (DSC) and specific surface area (SSA) analyses. Results show that KClO4 prepared by this method is coated on the surface of CNTs effectively. In comparion with pure CNTs, the diameter of CNTs supporting KClO4 increases significantly and the SSA of the CNTs/KClO4 composite decreases by 40.719 m2·g-1. In comparion with KClO4, the thermal decomposition temperature of the composite decreases by 75°C and crystal transformation peak temperature decrease by 5°C. In comparion with Mo/KClO4, the thermal conductivity of Mo/KClO4 ignition composition prepared by CNTs/KClO4 increases by 33.9%.",

keywords = "Carbon nano-tube (CNT), Coat, Composite materials, Physical chemistry, Potassium perchlorate (KClO)",

author = "Zhang, {Bu Yun} and Jiao, {Qing Jie} and Hui Ren and Jia, {Yong Jie} and Kuo Zhang and Wu, {Guan Nan} and Liu, {Guo Quan}",

year = "2011",

month = aug,

doi = "10.3969/j.issn.1006-9941.2011.04.011",

language = "English",

volume = "19",

pages = "401--404",

journal = "Hanneng Cailiao/Chinese Journal of Energetic Materials",

issn = "1006-9941",

publisher = "Chinese Academy of Engineering Physics",

number = "4",

}

TY - JOUR

T1 - Morphology character and thermal behavior of CNTs/KClO4

AU - Zhang, Bu Yun

AU - Jiao, Qing Jie

AU - Ren, Hui

AU - Jia, Yong Jie

AU - Zhang, Kuo

AU - Wu, Guan Nan

AU - Liu, Guo Quan

PY - 2011/8

Y1 - 2011/8

N2 - The carbon nano-tubes/potassium perchlorate (CNTs/KClO4) composite was prepared via a double decomposition reaction of NH4ClO4 solution and KOH solution in the presence of carbon nano-tubes. Morphology character and thermal behavior of the composite were studied by scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimeter (DSC) and specific surface area (SSA) analyses. Results show that KClO4 prepared by this method is coated on the surface of CNTs effectively. In comparion with pure CNTs, the diameter of CNTs supporting KClO4 increases significantly and the SSA of the CNTs/KClO4 composite decreases by 40.719 m2·g-1. In comparion with KClO4, the thermal decomposition temperature of the composite decreases by 75°C and crystal transformation peak temperature decrease by 5°C. In comparion with Mo/KClO4, the thermal conductivity of Mo/KClO4 ignition composition prepared by CNTs/KClO4 increases by 33.9%.

AB - The carbon nano-tubes/potassium perchlorate (CNTs/KClO4) composite was prepared via a double decomposition reaction of NH4ClO4 solution and KOH solution in the presence of carbon nano-tubes. Morphology character and thermal behavior of the composite were studied by scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimeter (DSC) and specific surface area (SSA) analyses. Results show that KClO4 prepared by this method is coated on the surface of CNTs effectively. In comparion with pure CNTs, the diameter of CNTs supporting KClO4 increases significantly and the SSA of the CNTs/KClO4 composite decreases by 40.719 m2·g-1. In comparion with KClO4, the thermal decomposition temperature of the composite decreases by 75°C and crystal transformation peak temperature decrease by 5°C. In comparion with Mo/KClO4, the thermal conductivity of Mo/KClO4 ignition composition prepared by CNTs/KClO4 increases by 33.9%.

KW - Carbon nano-tube (CNT)

KW - Coat

KW - Composite materials

KW - Physical chemistry

KW - Potassium perchlorate (KClO)

UR - http://www.scopus.com/inward/record.url?scp=80053079686&partnerID=8YFLogxK

U2 - 10.3969/j.issn.1006-9941.2011.04.011

DO - 10.3969/j.issn.1006-9941.2011.04.011

M3 - Article

AN - SCOPUS:80053079686

SN - 1006-9941

VL - 19

SP - 401

EP - 404

JO - Hanneng Cailiao/Chinese Journal of Energetic Materials

JF - Hanneng Cailiao/Chinese Journal of Energetic Materials

IS - 4

ER -

Morphology character and thermal behavior of CNTs/KClO4

摘要

访问文件

其它文件与链接

指纹

引用此

Morphology character and thermal behavior of CNTs/KClO₄