Mechanical and thermal properties and flame retardancy of phosphorus-containing polyhedral oligomeric silsesquioxane (DOPO-POSS)/ polycarbonate composites

Wenchao Zhang, Xiangmei Li, Xiaoyan Guo, Rongjie Yang*

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

145 引用 (Scopus)

摘要

A novel polyhedral oligomeric silsesquioxane containing 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO-POSS) has been incorporated into polycarbonate (PC) composites in order to study its effect on mechanical and thermal properties and flame retardancy. The mechanical and thermal properties of the DOPO-POSS/PC composites have been investigated by tensile and flexural testing, DSC, and DMA. Slight enhancements of yield stress, and flexural strength and modulus, and obvious decreases of fracture strength and strain of the DOPO-POSS/PC composites were observed with an increase in DOPO-POSS loading. The glass transition temperatures (Tg) of the composites were reduced with increasing DOPO-POSS loading. The morphology of the PC composites was evaluated by SEM, which indicated that the DOPO-POSS was dispersed with a particle size of 100-250 nm in the PC matrix. The thermal degradation behaviour and flame retardancies of PC composites with different DOPO-POSS loadings were investigated by TGA, LOI, UL-94 standard, and cone calorimetry. The composite had an LOI value of 30.5 and a UL-94 rating V-0 when the content of DOPO-POSS was 4%.

源语言英语
页(从-至)2541-2546
页数6
期刊Polymer Degradation and Stability
95
12
DOI
出版状态已出版 - 12月 2010

指纹

探究 'Mechanical and thermal properties and flame retardancy of phosphorus-containing polyhedral oligomeric silsesquioxane (DOPO-POSS)/ polycarbonate composites' 的科研主题。它们共同构成独一无二的指纹。

引用此