In-situ synthesis and growth mechanism of silicon nitride nanowires on carbon fiber fabrics

Kaiyuan Li; Ke Zhao; Yiguang Wang

doi:10.1016/j.ceramint.2014.05.058

In-situ synthesis and growth mechanism of silicon nitride nanowires on carbon fiber fabrics

Kaiyuan Li, Ke Zhao, Yiguang Wang^*

^*此作品的通讯作者

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

28 引用（Scopus）

摘要

Silicon nitride (Si₃N₄) nanowires were in-situ fabricated on carbon fiber fabrics up to 5 cm×11 cm in area via catalyst-assisted pyrolysis of polymeric precursors. The obtained products were randomly oriented around the carbon fibers with the diameter of 30-150 nm and the length of several hundred micrometers. The effects of process parameters including the preparation temperature, flow rate of nitrogen, catalyst proportion, and volume fraction of acetone on the synthesis of Si₃N₄ nanowires were discussed. Accordingly, a set of optimized process parameters was determined. The microstructure of the nanowires indicated that their formation obeyed a solid-liquid-gas-solid (SLGS) growth mechanism.

源语言	英语
页（从-至）	15381-15389
页数	9
期刊	Ceramics International
卷	40
期	10
DOI	https://doi.org/10.1016/j.ceramint.2014.05.058
出版状态	已出版 - 1 12月 2014
已对外发布	是

访问文件

10.1016/j.ceramint.2014.05.058

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{853a20d4f5714f96b4c4fedaed1fb566,

title = "In-situ synthesis and growth mechanism of silicon nitride nanowires on carbon fiber fabrics",

abstract = "Silicon nitride (Si3N4) nanowires were in-situ fabricated on carbon fiber fabrics up to 5 cm×11 cm in area via catalyst-assisted pyrolysis of polymeric precursors. The obtained products were randomly oriented around the carbon fibers with the diameter of 30-150 nm and the length of several hundred micrometers. The effects of process parameters including the preparation temperature, flow rate of nitrogen, catalyst proportion, and volume fraction of acetone on the synthesis of Si3N4 nanowires were discussed. Accordingly, a set of optimized process parameters was determined. The microstructure of the nanowires indicated that their formation obeyed a solid-liquid-gas-solid (SLGS) growth mechanism.",

keywords = "Carbon fiber fabric, Growth mechanism, In-situ synthesis, SiN nanowire",

author = "Kaiyuan Li and Ke Zhao and Yiguang Wang",

year = "2014",

month = dec,

day = "1",

doi = "10.1016/j.ceramint.2014.05.058",

language = "English",

volume = "40",

pages = "15381--15389",

journal = "Ceramics International",

issn = "0272-8842",

publisher = "Elsevier Ltd.",

number = "10",

}

TY - JOUR

T1 - In-situ synthesis and growth mechanism of silicon nitride nanowires on carbon fiber fabrics

AU - Li, Kaiyuan

AU - Zhao, Ke

AU - Wang, Yiguang

PY - 2014/12/1

Y1 - 2014/12/1

N2 - Silicon nitride (Si3N4) nanowires were in-situ fabricated on carbon fiber fabrics up to 5 cm×11 cm in area via catalyst-assisted pyrolysis of polymeric precursors. The obtained products were randomly oriented around the carbon fibers with the diameter of 30-150 nm and the length of several hundred micrometers. The effects of process parameters including the preparation temperature, flow rate of nitrogen, catalyst proportion, and volume fraction of acetone on the synthesis of Si3N4 nanowires were discussed. Accordingly, a set of optimized process parameters was determined. The microstructure of the nanowires indicated that their formation obeyed a solid-liquid-gas-solid (SLGS) growth mechanism.

AB - Silicon nitride (Si3N4) nanowires were in-situ fabricated on carbon fiber fabrics up to 5 cm×11 cm in area via catalyst-assisted pyrolysis of polymeric precursors. The obtained products were randomly oriented around the carbon fibers with the diameter of 30-150 nm and the length of several hundred micrometers. The effects of process parameters including the preparation temperature, flow rate of nitrogen, catalyst proportion, and volume fraction of acetone on the synthesis of Si3N4 nanowires were discussed. Accordingly, a set of optimized process parameters was determined. The microstructure of the nanowires indicated that their formation obeyed a solid-liquid-gas-solid (SLGS) growth mechanism.

KW - Carbon fiber fabric

KW - Growth mechanism

KW - In-situ synthesis

KW - SiN nanowire

UR - http://www.scopus.com/inward/record.url?scp=84912523540&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2014.05.058

DO - 10.1016/j.ceramint.2014.05.058

M3 - Article

AN - SCOPUS:84912523540

SN - 0272-8842

VL - 40

SP - 15381

EP - 15389

JO - Ceramics International

JF - Ceramics International

IS - 10

ER -

In-situ synthesis and growth mechanism of silicon nitride nanowires on carbon fiber fabrics

摘要

访问文件

其它文件与链接

指纹

引用此