Experimental Study at the Phase Interface of a Single-Crystal Ni-Based Superalloy Using TEM

Hongye Zhang*, Huihui Wen, Runlai Peng, Ruijun He, Miao Li, Wei Feng, Yao Zhao, Zhanwei Liu*

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

2 引用 (Scopus)

摘要

The single-crystal Ni-based superalloys, which have excellent mechanical properties at high temperatures, are commonly used for turbine blades in a variety of aero engines and industrial gas turbines. Focusing on the phase interface of a second-generation single-crystal Ni-based superalloy, in-situ TEM observation was conducted at room temperature and high temperatures. Intensity ratio analysis was conducted for the measurement of two-phase interface width. The improved geometric phase analysis method, where the adaptive mask selection method is introduced, was used for the measurement of the strain field near the phase interface. The strained irregular transition region is consistent with the calculated interface width using intensity ratio analysis. An intensity ratio analysis and strain measurement near the interface can corroborate and complement each other, contributing to the interface structure evaluation. Using TEM in-situ heating and Fourier transform, the change of dislocation density in the γ phase near the two-phase interface of the single-crystal Ni-based superalloy was analyzed. The dislocation density decreases first with the increase in temperature, consistent with the characteristics of metal quenching, and increases sharply at 450 °C. The correlation between the variation of dislocation density at high temperatures and the intermediate temperature brittleness was also investigated.

源语言英语
文章编号6915
期刊Materials
15
19
DOI
出版状态已出版 - 10月 2022

指纹

探究 'Experimental Study at the Phase Interface of a Single-Crystal Ni-Based Superalloy Using TEM' 的科研主题。它们共同构成独一无二的指纹。

引用此