Enhanced Cyclability of C/Lithium Iron Phosphate Cathodes with a Novel water-soluble lithium-ion binder

Novel cellulose-derived lithium carboxymethyl cellulose (CMC-Li) was synthesized using cotton as the raw material. Properties of electrospun CMC-Li-modified electrode materials and CMC-Li binders are described in this study. CMC-Li/Lithium Iron Phosphate (LiFePO₄, LFP) composite fibers and CMC-Li nanofibers were successfully obtained by electrospinning. Next, CMC-Li/LFP nano-composite fibers were carbonized under nitrogen at a high-temperature to form carbon nanofibers (CNFs), and carbon nanofiber/lithium iron phosphate/lithium-Ion compound (CNF/LFP/Li, CLL) composite nanofibers were formed as the cathode material. CMC-Li was investigated as a novel water-soluble binder. Compared with conventional poly (vinylidene fluoride) (PVDF) binders, the CMC-Li binder significantly improved cycling performance of the LFP cathode with 97.5% of retention of initial reversible capacity after 200 cycles at 175 mAh g^-1. Constant current charge-discharge test results demonstrated that the CLL electrodes with CMC-Li binders have the highest rate capability of those tested in this study. This approach enables increased Li⁺ contents with improved diffusion efficiency and specific capacity. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), X-ray diffraction (XRD) and scanning electron microscopy (SEM) were utilized to characterize material performance. The batteries demonstrated good electrochemical properties, excellent stability and outstanding pollution-free performance.