Effect of interface behaviour on damage and instability of PBX under combined tension–shear loading

Quan zhi Xia, Yan qing Wu*, Feng lei Huang

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

15 引用 (Scopus)

摘要

To study the effect of interface behaviour on the mechanical properties and damage evolution of PBX under combined tension–shear loading, the present work establishes the numerical model of a PBX three-phase hybrid system, which introduces a nonlinear plastic damage cohesion model to study the mechanical response and damage process. The parameters in the model were fitted and calibrated. Taking the crack growth rate as the feature, the damage state in each stage was determined, and the damage instability criterion was given. The effects of interfacial tensile strength and shear strength on the damage process of PBX were studied. On this basis, serrated and hemispherical structures interface of PBX has been developed, which affects the damage process and instability during the loading process. The results indicate that damage state response of PBX experiences the process of stable load bearing, unstable propagation, and complete failure. At the critical moment of instability, the overall equivalent effective strain of material reaches 3024 με and instability loading displacement reaches 0.39 mm. The increase of interfacial tensile strength and shear strength significantly inhibits the damage of PBX. The effect of interfacial shear strength on critical instability of PBX is approximately 1.7 times that of the interfacial tensile strength. Further, interface opening along the normal direction is the main damage form at the interface. Serrated and hemispherical rough interfaces can significantly inhibit propagation of cracks, and the load bearing capacity is improved by 22% and 9.7%, respectively. Appropriate improvement of the roughness of the interface structure can effectively improve the mechanical properties. It is significantly important to have a better understanding of deformation, damage and failure mechanisms of PBX and to improve our predictive ability.

源语言英语
页(从-至)137-151
页数15
期刊Defence Technology
23
DOI
出版状态已出版 - 5月 2023

指纹

探究 'Effect of interface behaviour on damage and instability of PBX under combined tension–shear loading' 的科研主题。它们共同构成独一无二的指纹。

引用此