TY - JOUR
T1 - Bu-NENA基改性 基推进剂的力学性能 安全性
AU - Sun, Shi Xiong
AU - Zhao, Ben Bo
AU - Sang, Chao
AU - Cheng, Yuan
AU - Luo, Yun Jun
N1 - Publisher Copyright:
© 2022 China Ordnance Industry Corporation. All rights reserved.
PY - 2022
Y1 - 2022
N2 - A novel double-base propellant plasticized by Bu-NENA which substitutes NG with high solid content was prepared by solvent-free process to improve mechanical and security performance. The tensile mechanical performance, dynamic mechanical properties, and mechanical sensitivities were tested by universal tensile tester, dynamic thermomechanical analyzer and sensitive testers. The results showed that, compared with NG, Bu-NENA can obviously decrease mechanical sensitivity and enhance mechanical properties of propellant. When the mass fraction of Bu-NENA is 19.1%, the mechanical properties of the propellant(code B3)are better. By contract with the blank group(NG based double base propellant, B0), the elongation under -40℃ was promoted by 114% from 3.5% to 7.57%. Friction sensitivity was decreased by 95.7% from 46% to 2%, meanwhile, H50 was increased by 95.3% from 17.2cm to 33.6cm. The study of dynamic mechanical properties shows that Bu-NENA has better plasticizing effect on nitrocellulose(NC). The β transition temperature of B3 propellant decreases from -33.8℃ of B0 to -37.8℃, and the toughness increases. The Bu-NENA based propellant exhibited an excellent low temperature mechanical property and low sensitivity which has certain application prospect in short range tactical weapon.
AB - A novel double-base propellant plasticized by Bu-NENA which substitutes NG with high solid content was prepared by solvent-free process to improve mechanical and security performance. The tensile mechanical performance, dynamic mechanical properties, and mechanical sensitivities were tested by universal tensile tester, dynamic thermomechanical analyzer and sensitive testers. The results showed that, compared with NG, Bu-NENA can obviously decrease mechanical sensitivity and enhance mechanical properties of propellant. When the mass fraction of Bu-NENA is 19.1%, the mechanical properties of the propellant(code B3)are better. By contract with the blank group(NG based double base propellant, B0), the elongation under -40℃ was promoted by 114% from 3.5% to 7.57%. Friction sensitivity was decreased by 95.7% from 46% to 2%, meanwhile, H50 was increased by 95.3% from 17.2cm to 33.6cm. The study of dynamic mechanical properties shows that Bu-NENA has better plasticizing effect on nitrocellulose(NC). The β transition temperature of B3 propellant decreases from -33.8℃ of B0 to -37.8℃, and the toughness increases. The Bu-NENA based propellant exhibited an excellent low temperature mechanical property and low sensitivity which has certain application prospect in short range tactical weapon.
KW - Bu-NENA
KW - energetic plasticizer
KW - high solid content
KW - modified double base propellant
KW - physical chemistry
UR - http://www.scopus.com/inward/record.url?scp=85139319028&partnerID=8YFLogxK
U2 - 10.14077/j.issn.1007-7812.202205008
DO - 10.14077/j.issn.1007-7812.202205008
M3 - 文章
AN - SCOPUS:85139319028
SN - 1007-7812
VL - 45
SP - 561
EP - 566
JO - Huozhayao Xuebao/Chinese Journal of Explosives and Propellants
JF - Huozhayao Xuebao/Chinese Journal of Explosives and Propellants
IS - 4
ER -