TY - JOUR
T1 - 高固含量磺酸型水性聚氨酯的制备与性能
AU - Hou, Jinghui
AU - Zhang, Zihan
AU - Ma, Yifei
AU - Chai, Chunpeng
N1 - Publisher Copyright:
© 2020, Editorial Board of Polymer Materials Science & Engineering. All right reserved.
PY - 2020/1/1
Y1 - 2020/1/1
N2 - Sulfonic waterborne polyurethane with high solid content were prepared by two kinds of emulsification with isophorone diisocyanate (IPDI), poly(1, 6-hexanediol/neopentyl glycol-adipic acid) (PHNA), 1, 4-butanediol (BDO), aqueous solution of sodium ethylenediamineethanesulfonate (AAS) (50%) was used as main raw material and triethylamine (TEA) was used as neutralizer. The results show that the emulsion dispersion method can obtain a higher solid content emulsion than the direct method. When the AAS content is 2.2%, the solid content of emulsion can reach more than 60%. The transmission electron microscope image of the emulsion shows that the emulsion dispersion method can well design and control the particle size of the emulsion. Particles with smaller particle size and more hard segments can be introduced by the emulsion dispersion method, the physical crosslinking points are increased and the film becomes denser. When the content of AAS is 2.2%, the water absorption rate of the adhesive film obtained by the emulsion dispersion method is 33.71%, the tensile strength is 9.90 MPa, and the elongation at break is 1262%. Compared with the direct method, the water absorption rate of the film is decreased by 66.24%, the tensile strength is increased by 0.61 MPa, and the elongation at break is reduced by 110%.
AB - Sulfonic waterborne polyurethane with high solid content were prepared by two kinds of emulsification with isophorone diisocyanate (IPDI), poly(1, 6-hexanediol/neopentyl glycol-adipic acid) (PHNA), 1, 4-butanediol (BDO), aqueous solution of sodium ethylenediamineethanesulfonate (AAS) (50%) was used as main raw material and triethylamine (TEA) was used as neutralizer. The results show that the emulsion dispersion method can obtain a higher solid content emulsion than the direct method. When the AAS content is 2.2%, the solid content of emulsion can reach more than 60%. The transmission electron microscope image of the emulsion shows that the emulsion dispersion method can well design and control the particle size of the emulsion. Particles with smaller particle size and more hard segments can be introduced by the emulsion dispersion method, the physical crosslinking points are increased and the film becomes denser. When the content of AAS is 2.2%, the water absorption rate of the adhesive film obtained by the emulsion dispersion method is 33.71%, the tensile strength is 9.90 MPa, and the elongation at break is 1262%. Compared with the direct method, the water absorption rate of the film is decreased by 66.24%, the tensile strength is increased by 0.61 MPa, and the elongation at break is reduced by 110%.
KW - Emulsion dispersion method
KW - High solid content
KW - Sulfonic
KW - Waterborne polyurethane
UR - http://www.scopus.com/inward/record.url?scp=85081655033&partnerID=8YFLogxK
U2 - 10.16865/j.cnki.1000-7555.2019.0350
DO - 10.16865/j.cnki.1000-7555.2019.0350
M3 - 文章
AN - SCOPUS:85081655033
SN - 1000-7555
VL - 36
SP - 152
EP - 158
JO - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering
JF - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering
IS - 1
ER -