TY - JOUR
T1 - Synthesis and Properties of Octet NiCr Alloy Lattices Obtained by the Pack Cementation Process
AU - Zhao, Peng
AU - Huang, Deqing
AU - Zhang, Hongmei
AU - Chen, Weiwei
AU - Zhang, Yongfu
N1 - Publisher Copyright:
© 2023 by the authors.
PY - 2023/2
Y1 - 2023/2
N2 - NiCr alloys with different components were obtained by pack chromation and homogenization heat treatment of octet Ni lattice. The microstructure, alloy composition, microhardness and quasi-static compression properties of the NiCr lattice were tested. The results showed that after homogenization heat treatment, the NiCr alloy lattice had an austenitic structure with uniform composition. Compared with the pure nickel lattice, the microhardness, compressive strength, elastic modulus and energy absorption of the NiCr lattice increased with the increase of chromium content. The microhardness, specific strength, specific modulus and specific energy absorption of the Ni-45Cr alloy were 363 HV, 11.1 MP/(g/cm3), 1169.1 MP/(g/cm3) and 10 J/g, respectively, which were attributed to the solid solution strengthening provided by chromium and the increase in density. NiCr alloy lattices have high strength and toughness and may have potential applications in high-temperature filters or heat exchangers.
AB - NiCr alloys with different components were obtained by pack chromation and homogenization heat treatment of octet Ni lattice. The microstructure, alloy composition, microhardness and quasi-static compression properties of the NiCr lattice were tested. The results showed that after homogenization heat treatment, the NiCr alloy lattice had an austenitic structure with uniform composition. Compared with the pure nickel lattice, the microhardness, compressive strength, elastic modulus and energy absorption of the NiCr lattice increased with the increase of chromium content. The microhardness, specific strength, specific modulus and specific energy absorption of the Ni-45Cr alloy were 363 HV, 11.1 MP/(g/cm3), 1169.1 MP/(g/cm3) and 10 J/g, respectively, which were attributed to the solid solution strengthening provided by chromium and the increase in density. NiCr alloy lattices have high strength and toughness and may have potential applications in high-temperature filters or heat exchangers.
KW - mechanical properties
KW - nickel-based lattice
KW - pack cementation
KW - solution strengthening
UR - http://www.scopus.com/inward/record.url?scp=85148035717&partnerID=8YFLogxK
U2 - 10.3390/app13031684
DO - 10.3390/app13031684
M3 - Article
AN - SCOPUS:85148035717
SN - 2076-3417
VL - 13
JO - Applied Sciences (Switzerland)
JF - Applied Sciences (Switzerland)
IS - 3
M1 - 1684
ER -