T1 - Piezoelectric ceramics in the PbSnO3-Pb(Mg1/3Nb 2/3)O3-PbTiO3 ternary system
AU - Wang, Dawei
AU - Cao, Maosheng
AU - Zhang, Shujun
PY - 2011/11
Y1 - 2011/11
N2 - Piezoelectric ceramics in the ternary system (0.8-x)PbSnO 3-0.2Pb(Mg1/3Nb2/3)O3-xPbTiO 3 (PSn-PMN-PT, x = 0.42-0.47) were synthesized. Morphotropic phase boundary (MPB) compositions, located at ∼PT = 0.43-0.45 were confirmed by X-ray diffraction, dielectric, piezoelectric, and ferroelectric properties. The coercive field EC, internal bias field Ei, and mechanical quality factor Qm were found to increase with increasing PT content, indicative of piezoelectric "hardening" characteristics, while the optimum dielectric and piezoelectric properties were achieved for the MPB composition 0.36PSn-0.2PMN-0.44PT, with dielectric permittivity εr, piezoelectric coefficient d33, and planar electromechanical coupling kp being on the order of 2930, 510 pC/N and 55%, respectively. In addition, the aging behavior of the piezoelectric ceramics was studied, with aging rate of d33 ∼-6%, kp ∼-2%, εr ∼-7% per decade, respectively, similar to commercial PZT4 ceramics.
AB - Piezoelectric ceramics in the ternary system (0.8-x)PbSnO 3-0.2Pb(Mg1/3Nb2/3)O3-xPbTiO 3 (PSn-PMN-PT, x = 0.42-0.47) were synthesized. Morphotropic phase boundary (MPB) compositions, located at ∼PT = 0.43-0.45 were confirmed by X-ray diffraction, dielectric, piezoelectric, and ferroelectric properties. The coercive field EC, internal bias field Ei, and mechanical quality factor Qm were found to increase with increasing PT content, indicative of piezoelectric "hardening" characteristics, while the optimum dielectric and piezoelectric properties were achieved for the MPB composition 0.36PSn-0.2PMN-0.44PT, with dielectric permittivity εr, piezoelectric coefficient d33, and planar electromechanical coupling kp being on the order of 2930, 510 pC/N and 55%, respectively. In addition, the aging behavior of the piezoelectric ceramics was studied, with aging rate of d33 ∼-6%, kp ∼-2%, εr ∼-7% per decade, respectively, similar to commercial PZT4 ceramics.
UR - http://www.scopus.com/inward/record.url?scp=80155168609&partnerID=8YFLogxK
U2 - 10.1111/j.1551-2916.2011.04857.x
DO - 10.1111/j.1551-2916.2011.04857.x
M3 - Article
AN - SCOPUS:80155168609
SN - 0002-7820
VL - 94
SP - 3690
EP - 3693
JO - Journal of the American Ceramic Society
JF - Journal of the American Ceramic Society
IS - 11
ER -