Investigation into the effect of molybdenum-site substitution on the performance of Sr₂Fe_1.5Mo_0.5O_6-δ for intermediate temperature solid oxide fuel cells

In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr₂Fe_1.5Mo_0.5O_6-δ (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr₂Fe_1.5Mo_0.5-xNb_xO_6-δ (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr₂Fe_1.5Mo_0.4Nb_0.10O_6-δ (SFMNb_0.10) exhibits the highest conductivity value of 30 S cm^-1 at 550°C, and the lowest area specific resistance of 0.068 Ω cm² at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb_0.10 cathode presents a maximum power density of 1102 mW cm^-2 at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H₂(3% H₂O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.