Electromagnetic absorption properties of Fe_xCoNi magnetic nano particles

The microstructure morphology, static magnetic properties, and electromagnetic absorption characteristics of nano FexCoNi alloy particles prepared by chemical liquid deposition with five different Fe content levels are investigated in this paper. The results show that spherical FexCoNi alloy particles with an average particle size of about 100-200 nm and a face-centered cubic crystal structure were obtained. All five samples exhibited soft magnetic behavior, with the saturation magnetization intensity showing an increasing-then-decreasing trend with increasing Fe content, peaking at 141.8 emu/g for Fe content x = 1.0. The dielectric constants (real and imaginary parts) of the prepared alloy particles exhibit significant differences with respect to the variation of Fe content, while the changes in the real and imaginary parts of the magnetic permeability show less pronounced effects with increasing Fe content. As the electromagnetic wave frequency increases, the real parts of the dielectric constants for all composites show minimal fluctuations, and the real parts of the magnetic permeability exhibit a decreasing trend. Moreover, the imaginary parts of the dielectric constants and magnetic permeability show an increasing followed by a decreasing trend as the frequency rises. The material with Fe content x = 1 demonstrated optimal dielectric loss performance and relatively excellent magnetic loss performance, with a sample thickness of 1.9 mm exhibiting the highest reflection loss (RLmax) of −24.2 dB and an effective absorption bandwidth of 4.48 GHz.