T1 - Characterization of LiNbO3 nanocrystals prepared via a convenient hydrothermal route
AU - An, Changhua
AU - Tang, Kaibin
AU - Wang, Chunrui
AU - Shen, Guozhen
AU - Jin, Ying
AU - Qian, Yitai
PY - 2002/9
Y1 - 2002/9
N2 - LiNbO3 nanocrystal was successfully prepared via a simple and convenient hydrothermal route using LiOH and Nb2O5 as the reactants. Transmission electron microscopy images shows that the as-prepared sample displays a flake-like shape of 40-100 nm. X-ray diffraction, IR spectrum and Raman spectra of the as-prepared sample indicates that the sample was well crystalline and of high purity.
AB - LiNbO3 nanocrystal was successfully prepared via a simple and convenient hydrothermal route using LiOH and Nb2O5 as the reactants. Transmission electron microscopy images shows that the as-prepared sample displays a flake-like shape of 40-100 nm. X-ray diffraction, IR spectrum and Raman spectra of the as-prepared sample indicates that the sample was well crystalline and of high purity.
KW - A. Inorganic compounds
KW - B. Chemical synthesis
KW - C. X-ray diffraction
KW - D. Crystal structure
UR - http://www.scopus.com/inward/record.url?scp=0036712923&partnerID=8YFLogxK
U2 - 10.1016/S0025-5408(02)00869-3
DO - 10.1016/S0025-5408(02)00869-3
M3 - Article
AN - SCOPUS:0036712923
SN - 0025-5408
VL - 37
SP - 1791
EP - 1796
JO - Materials Research Bulletin
JF - Materials Research Bulletin
IS - 11
ER -