T1 - 基于红外光谱的HTPB推进剂老化机理
AU - Wang, Xinyuan
AU - Zhang, Yajun
AU - Sui, Xin
AU - Tao, Tao
N1 - Publisher Copyright:
© 2019, Editorial Dept. of JSRT. All right reserved.
PY - 2019/8/1
Y1 - 2019/8/1
N2 - In order to study the aging characteristic mechanism of HTPB propellant from the perspective of infrared spectrum,the accelerated aging test of HTPB propellant at 70 ℃ was carried out,moreover the maximum elongation and infrared absorption spectrum were measured at 15 different aging time.By analyzing the relevance between the changes of absorption spectrum and the maximum elongation of the samples, infrared characteristic wave number closely related to elongation and its corresponding characteristic functional groups -OH,〖JG(〗C〖ZJLX,Y〗O,〖JG)〗and NH4 +were found,moreover both characteristic absorption peak intensity and maximum elongation present a general downward tendency.The results show that during accelerated aging process, the main aging mechanism of HTPB propellant samples is post-curing reaction consuming -OH,〖JG(〗C〖ZJLX,Y〗O,〖JG)〗and oxidative crosslinking reaction resulting in reduction of NH4 + content. At the same time,thess results are consistent with those obtained from traditional methods,which indicates that infrared spectroscopy will become a tool quantitatively reflects aging properties of HTPB propellant.
AB - In order to study the aging characteristic mechanism of HTPB propellant from the perspective of infrared spectrum,the accelerated aging test of HTPB propellant at 70 ℃ was carried out,moreover the maximum elongation and infrared absorption spectrum were measured at 15 different aging time.By analyzing the relevance between the changes of absorption spectrum and the maximum elongation of the samples, infrared characteristic wave number closely related to elongation and its corresponding characteristic functional groups -OH,〖JG(〗C〖ZJLX,Y〗O,〖JG)〗and NH4 +were found,moreover both characteristic absorption peak intensity and maximum elongation present a general downward tendency.The results show that during accelerated aging process, the main aging mechanism of HTPB propellant samples is post-curing reaction consuming -OH,〖JG(〗C〖ZJLX,Y〗O,〖JG)〗and oxidative crosslinking reaction resulting in reduction of NH4 + content. At the same time,thess results are consistent with those obtained from traditional methods,which indicates that infrared spectroscopy will become a tool quantitatively reflects aging properties of HTPB propellant.
KW - Accelerated aging test
KW - Aging mechanism
KW - Elongation
KW - HTPB propellant
KW - Infrared spectrum
UR - http://www.scopus.com/inward/record.url?scp=85072190645&partnerID=8YFLogxK
U2 - 10.7673/j.issn.1006-2793.2019.04.009
DO - 10.7673/j.issn.1006-2793.2019.04.009
M3 - 文章
AN - SCOPUS:85072190645
SN - 1006-2793
VL - 42
SP - 471
EP - 475
JO - Guti Huojian Jishu/Journal of Solid Rocket Technology
JF - Guti Huojian Jishu/Journal of Solid Rocket Technology
IS - 4
ER -