Synthesis and electrochemical performance of LiNi0.5Mn 1.5O4 spinel compound

G. Q. Liu; Y. J. Wang; Qilu; W. Li; Chenhui

doi:10.1016/j.electacta.2004.08.047

Synthesis and electrochemical performance of LiNi_0.5Mn _1.5O₄ spinel compound

G. Q. Liu, Y. J. Wang, Qilu^*, W. Li, Chenhui

^*此作品的通讯作者

材料学院

Peking University

科研成果: 期刊稿件 › 文章 › 同行评审

36 引用（Scopus）

摘要

Spinel compound LiNi_0.5Mn_1.5O₄ was synthesized by a chemical wet method. Mn(NO₃)₂, Ni(NO ₃)₂·6H₂O, NH₄HCO₃ and LiOH·H₂O were used as the starting materials. At first, Mn(NO₃)₂ and Ni(NO₃)₂·6H ₂O reacted with NH₄HCO₃ to produce a precursor, then the precursor reacted with LiOH·H₂O to synthesize product LiNi_0.5Mn_1.5O₄. The product showed a single spinel phase under appropriate calcination conditions, and exhibited a high voltage plateau at about 4.6-4.8 V in the charge/discharge process. The LiNi_0.5Mn_1.5O₄ had a discharge specific capacity of 118 mAh/g at about 4.6 V and 126 mAh/g in total in the first cycle at a discharge current density of 2 mA/cm². After 50 cycles, the total discharge capacity was above 118 mAh/g.

源语言	英语
页（从-至）	1965-1968
页数	4
期刊	Electrochimica Acta
卷	50
期	9
DOI	https://doi.org/10.1016/j.electacta.2004.08.047
出版状态	已出版 - 1 3月 2005

访问文件

10.1016/j.electacta.2004.08.047

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{1bd8d9d92f804230a02fa5f4208095f6,

title = "Synthesis and electrochemical performance of LiNi0.5Mn 1.5O4 spinel compound",

abstract = "Spinel compound LiNi0.5Mn1.5O4 was synthesized by a chemical wet method. Mn(NO3)2, Ni(NO 3)2·6H2O, NH4HCO3 and LiOH·H2O were used as the starting materials. At first, Mn(NO3)2 and Ni(NO3)2·6H 2O reacted with NH4HCO3 to produce a precursor, then the precursor reacted with LiOH·H2O to synthesize product LiNi0.5Mn1.5O4. The product showed a single spinel phase under appropriate calcination conditions, and exhibited a high voltage plateau at about 4.6-4.8 V in the charge/discharge process. The LiNi0.5Mn1.5O4 had a discharge specific capacity of 118 mAh/g at about 4.6 V and 126 mAh/g in total in the first cycle at a discharge current density of 2 mA/cm2. After 50 cycles, the total discharge capacity was above 118 mAh/g.",

keywords = "Cathode, Electrochemical properties, Li-ion battery, LiNiMnO spinel, Synthesis",

author = "Liu, {G. Q.} and Wang, {Y. J.} and Qilu and W. Li and Chenhui",

year = "2005",

month = mar,

day = "1",

doi = "10.1016/j.electacta.2004.08.047",

language = "English",

volume = "50",

pages = "1965--1968",

journal = "Electrochimica Acta",

issn = "0013-4686",

publisher = "Elsevier Ltd.",

number = "9",

}

TY - JOUR

T1 - Synthesis and electrochemical performance of LiNi0.5Mn 1.5O4 spinel compound

AU - Liu, G. Q.

AU - Wang, Y. J.

AU - Qilu,

AU - Li, W.

AU - Chenhui,

PY - 2005/3/1

Y1 - 2005/3/1

N2 - Spinel compound LiNi0.5Mn1.5O4 was synthesized by a chemical wet method. Mn(NO3)2, Ni(NO 3)2·6H2O, NH4HCO3 and LiOH·H2O were used as the starting materials. At first, Mn(NO3)2 and Ni(NO3)2·6H 2O reacted with NH4HCO3 to produce a precursor, then the precursor reacted with LiOH·H2O to synthesize product LiNi0.5Mn1.5O4. The product showed a single spinel phase under appropriate calcination conditions, and exhibited a high voltage plateau at about 4.6-4.8 V in the charge/discharge process. The LiNi0.5Mn1.5O4 had a discharge specific capacity of 118 mAh/g at about 4.6 V and 126 mAh/g in total in the first cycle at a discharge current density of 2 mA/cm2. After 50 cycles, the total discharge capacity was above 118 mAh/g.

AB - Spinel compound LiNi0.5Mn1.5O4 was synthesized by a chemical wet method. Mn(NO3)2, Ni(NO 3)2·6H2O, NH4HCO3 and LiOH·H2O were used as the starting materials. At first, Mn(NO3)2 and Ni(NO3)2·6H 2O reacted with NH4HCO3 to produce a precursor, then the precursor reacted with LiOH·H2O to synthesize product LiNi0.5Mn1.5O4. The product showed a single spinel phase under appropriate calcination conditions, and exhibited a high voltage plateau at about 4.6-4.8 V in the charge/discharge process. The LiNi0.5Mn1.5O4 had a discharge specific capacity of 118 mAh/g at about 4.6 V and 126 mAh/g in total in the first cycle at a discharge current density of 2 mA/cm2. After 50 cycles, the total discharge capacity was above 118 mAh/g.

KW - Cathode

KW - Electrochemical properties

KW - Li-ion battery

KW - LiNiMnO spinel

KW - Synthesis

UR - http://www.scopus.com/inward/record.url?scp=13544253444&partnerID=8YFLogxK

U2 - 10.1016/j.electacta.2004.08.047

DO - 10.1016/j.electacta.2004.08.047

M3 - Article

AN - SCOPUS:13544253444

SN - 0013-4686

VL - 50

SP - 1965

EP - 1968

JO - Electrochimica Acta

JF - Electrochimica Acta

IS - 9

ER -

Synthesis and electrochemical performance of LiNi0.5Mn 1.5O4 spinel compound

摘要

访问文件

其它文件与链接

指纹

引用此

Synthesis and electrochemical performance of LiNi_0.5Mn _1.5O₄ spinel compound