Enhanced mechanical properties due to nanocrystallization by isothermal annealing in Al85Ni9Er6 glassy alloy

Jiaming Yin, Hongnian Cai, Xingwang Cheng*, Hongmei Zhang, Xinqiang Zhang, Ziqi Xu

*此作品的通讯作者

科研成果: 期刊稿件文章同行评审

7 引用 (Scopus)

摘要

In present work, isothermal annealing has been used to enhance the mechanical properties of Al85Ni9Er6 glassy alloy. Compared to 3.55 GPa, the hardness of the melt-spun alloy, the hardness of the alloy after annealed for 60 min and 90 min increased to 5.7 GPa and 5.55 GPa, respectively. The appearance of many fcc-Al nanocrystals lead to significant hardening. During the annealing, the nanocrystal size does not change much, but nanocrystal number increases between 50 min and 90 min at 519 K, which inferred that the mechanical properties of Al-based metallic glasses may be influenced by crystal number more than crystal size. The mechanical properties evolution of the metallic glass with the annealing time is due to combined effects of variations of the free volume and fcc-Al nanocrystals in the amorphous matrix.

源语言英语
页(从-至)3048-3053
页数6
期刊Journal of Alloys and Compounds
695
DOI
出版状态已出版 - 25 2月 2017

指纹

探究 'Enhanced mechanical properties due to nanocrystallization by isothermal annealing in Al85Ni9Er6 glassy alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此

Yin, J., Cai, H., Cheng, X., Zhang, H., Zhang, X., & Xu, Z. (2017). Enhanced mechanical properties due to nanocrystallization by isothermal annealing in Al85Ni9Er6 glassy alloy. Journal of Alloys and Compounds, 695, 3048-3053. https://doi.org/10.1016/j.jallcom.2016.11.346