T1 - Effects of Aluminum Content on Microstructure and Compressive Properties of TiAl Alloy
AU - Hao, Yanjun
AU - Liu, Jinxu
AU - Li, Jianchong
AU - Wang, Guohui
AU - Li, Shukui
AU - Chen, Dong
N1 - Publisher Copyright:
© 2017, Science Press. All right reserved.
PY - 2017/3/1
Y1 - 2017/3/1
N2 - The effects of aluminum content on microstructure and compressive properties of TiAl alloy were investigated, and the failure mechanism was also discussed. It is interesting to find that the content of aluminum remarkably influences the microstructure of TiAl alloys fabricated by Induction Skull Melting technique. The microstructure of Ti-44.1Al (at%, similarly hereinafter) alloy is fully lamellar, and the γ/α2 lamellar colonies exhibit the characteristics of columnar crystals. The microstructure of Ti-47.3Al alloy is duplex, which contains γ/α2 lamellar colonies and γ phase with 3D net structure. The microstructure of Ti-47.3Al alloy is much finer than that of Ti-44.1Al alloy. Compared with Ti-47.3Al alloy, Ti-44.1Al alloy exhibits higher yield strength, lower ultimate compressive strength, and lower ductility under both quasi-static compression and dynamic compression. Failure analysis after quasi-static compression shows that in Ti-44.1Al alloy, micro-pores initiation occurs in α2 phase of γ/α2 lamellar colonies. In Ti-47.3Al alloy, micro-pores initiation starts in both α2 phase of γ/α2 lamellar colonies and γ phase with 3D net structure. Thus, the failure mechanisms of both Ti-44.1Al alloy and Ti-47.3Al alloy are micro-porous coalescence fracture under quasi-static compression. Failure analysis after dynamic compression shows that in Ti-44.1Al alloy, micro-cracks originate in phase boundary between γ phase and α2 phase. In Ti-47.3Al alloy, micro-cracks originate in both phase boundary of γ/α2 lamellar colonies and γ phase with 3D net structure. With the increasing strain, the micro-cracks propagate rapidly, and cause the failure of the alloys under dynamic compression.
AB - The effects of aluminum content on microstructure and compressive properties of TiAl alloy were investigated, and the failure mechanism was also discussed. It is interesting to find that the content of aluminum remarkably influences the microstructure of TiAl alloys fabricated by Induction Skull Melting technique. The microstructure of Ti-44.1Al (at%, similarly hereinafter) alloy is fully lamellar, and the γ/α2 lamellar colonies exhibit the characteristics of columnar crystals. The microstructure of Ti-47.3Al alloy is duplex, which contains γ/α2 lamellar colonies and γ phase with 3D net structure. The microstructure of Ti-47.3Al alloy is much finer than that of Ti-44.1Al alloy. Compared with Ti-47.3Al alloy, Ti-44.1Al alloy exhibits higher yield strength, lower ultimate compressive strength, and lower ductility under both quasi-static compression and dynamic compression. Failure analysis after quasi-static compression shows that in Ti-44.1Al alloy, micro-pores initiation occurs in α2 phase of γ/α2 lamellar colonies. In Ti-47.3Al alloy, micro-pores initiation starts in both α2 phase of γ/α2 lamellar colonies and γ phase with 3D net structure. Thus, the failure mechanisms of both Ti-44.1Al alloy and Ti-47.3Al alloy are micro-porous coalescence fracture under quasi-static compression. Failure analysis after dynamic compression shows that in Ti-44.1Al alloy, micro-cracks originate in phase boundary between γ phase and α2 phase. In Ti-47.3Al alloy, micro-cracks originate in both phase boundary of γ/α2 lamellar colonies and γ phase with 3D net structure. With the increasing strain, the micro-cracks propagate rapidly, and cause the failure of the alloys under dynamic compression.
KW - Compressive properties
KW - Failure mechanism
KW - TiAl alloy
UR - http://www.scopus.com/inward/record.url?scp=85020101913&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:85020101913
SN - 1002-185X
VL - 46
SP - 754
EP - 759
JO - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
JF - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
IS - 3
ER -