Study on the in vitro degradation behavior of pure Mg and WE43 in human bile for 60 days for future usage in biliary

Mg and its alloys have been tested in both bone and blood environment, but the degradation process in human bile have not been reported yet. In this case, commercial pure Mg and WE43 alloy were investigated in human bile to see the corrosion performance as potential biliary stent materials. The results revealed the weight loss of WE43 after 60 days immersion was only 1.87%. Moreover, WE43 performed a superior corrosion resistance to pure Mg, owing to more formation of the secondary reaction product Mg(H₂PO₄)₂. The formation of H₂PO₄^- instead of PO₄^3- may be due to the fact that the compositions in the bile can prevent the formation of PO₄^3- as it is the main composition of gallstone. The much slower corrosion rate of the WE43 alloy in human bile indicated that it may be good candidates as biliary stent materials.