Studies on composite polymer electrolyte based on polypropene film and LiTFSI-acetamide molten salt

Ren Jie Chen; Feng Wu; Hong Ying Liang; Man Xie

Studies on composite polymer electrolyte based on polypropene film and LiTFSI-acetamide molten salt

Ren Jie Chen
, Feng Wu^*
, Hong Ying Liang
, Man Xie

^*此作品的通讯作者

Beijing Institute of Technology
High Technol. Green Mat. Devmt. Ctr.

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

The new low-temperature molten salt based on LiTFSI with acetamide has excellent thermal stability and electrochemical properties. A composite polymer electrolyte was prepared by dipping high strength porous-rich polypropene film in LiTFSI-acetamide molten salt. The conductive behavior of this CPE had been evaluated by using AC impedance spectroscopy, and the electrochemical window by cyclic voltammetry. This CPE exhibited not only outstanding thermal stability, but also higher ionic conductivity. The conductivity of CPE is 0.27×10^-3 S/cm at 25°C and 1.46×10^-3 S/cm at 60°C.

源语言	英语
页（从-至）	35-37
页数	3
期刊	Xiandai Huagong/Modern Chemical Industry
卷	23
期	12
出版状态	已出版 - 12月 2003
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{8018f3b9c40e4fe38097b10f3bc9baca,

title = "Studies on composite polymer electrolyte based on polypropene film and LiTFSI-acetamide molten salt",

abstract = "The new low-temperature molten salt based on LiTFSI with acetamide has excellent thermal stability and electrochemical properties. A composite polymer electrolyte was prepared by dipping high strength porous-rich polypropene film in LiTFSI-acetamide molten salt. The conductive behavior of this CPE had been evaluated by using AC impedance spectroscopy, and the electrochemical window by cyclic voltammetry. This CPE exhibited not only outstanding thermal stability, but also higher ionic conductivity. The conductivity of CPE is 0.27×10-3 S/cm at 25°C and 1.46×10-3 S/cm at 60°C.",

keywords = "Acetamide, Composite film, LiTFSI, Polymer electrolytes",

author = "Chen, \{Ren Jie\} and Feng Wu and Liang, \{Hong Ying\} and Man Xie",

year = "2003",

month = dec,

language = "English",

volume = "23",

pages = "35--37",

journal = "Xiandai Huagong/Modern Chemical Industry",

issn = "0253-4320",

publisher = "China National Chemical Information Center",

number = "12",

}

TY - JOUR

T1 - Studies on composite polymer electrolyte based on polypropene film and LiTFSI-acetamide molten salt

AU - Chen, Ren Jie

AU - Wu, Feng

AU - Liang, Hong Ying

AU - Xie, Man

PY - 2003/12

Y1 - 2003/12

N2 - The new low-temperature molten salt based on LiTFSI with acetamide has excellent thermal stability and electrochemical properties. A composite polymer electrolyte was prepared by dipping high strength porous-rich polypropene film in LiTFSI-acetamide molten salt. The conductive behavior of this CPE had been evaluated by using AC impedance spectroscopy, and the electrochemical window by cyclic voltammetry. This CPE exhibited not only outstanding thermal stability, but also higher ionic conductivity. The conductivity of CPE is 0.27×10-3 S/cm at 25°C and 1.46×10-3 S/cm at 60°C.

AB - The new low-temperature molten salt based on LiTFSI with acetamide has excellent thermal stability and electrochemical properties. A composite polymer electrolyte was prepared by dipping high strength porous-rich polypropene film in LiTFSI-acetamide molten salt. The conductive behavior of this CPE had been evaluated by using AC impedance spectroscopy, and the electrochemical window by cyclic voltammetry. This CPE exhibited not only outstanding thermal stability, but also higher ionic conductivity. The conductivity of CPE is 0.27×10-3 S/cm at 25°C and 1.46×10-3 S/cm at 60°C.

KW - Acetamide

KW - Composite film

KW - LiTFSI

KW - Polymer electrolytes

UR - https://www.scopus.com/pages/publications/1842534917

M3 - Article

AN - SCOPUS:1842534917

SN - 0253-4320

VL - 23

SP - 35

EP - 37

JO - Xiandai Huagong/Modern Chemical Industry

JF - Xiandai Huagong/Modern Chemical Industry

IS - 12

ER -

Studies on composite polymer electrolyte based on polypropene film and LiTFSI-acetamide molten salt

摘要

其它文件与链接

指纹

引用此