T1 - Sr14.06Gd14.63(BO3)24
T2 - A Gadolinium-Rich Borate with Magnetic Refrigeration Performance
AU - Chen, Yuwei
AU - Liu, Wang
AU - Wang, Dong
AU - Wang, Naizheng
AU - Fan, Feidi
AU - Shen, Jun
AU - Zhang, Guochun
AU - Song, Huimin
AU - Tu, Heng
N1 - Publisher Copyright:
© 2023 American Chemical Society.
PY - 2023/7/3
Y1 - 2023/7/3
N2 - A single crystal of Sr14.06Gd14.63(BO3)24 has been successfully grown through a high-temperature solution technique with K2O-KF-B2O3 as the flux. It crystallizes in the Pnma space group with parameters a = 22.3153(5) Å, b = 15.9087(4) Å, c = 8.7507(2) Å, and Z = 2. Sr14.06Gd14.63(BO3)24 has a three-dimensional (3D) framework built from [GdO] chains, in which the isolate [BO3]3- groups and Sr2+ ions fill in the space of the 3D framework. The magnetic measurements revealed that the title compound exhibits a large magnetocaloric effect with the magnetic entropy change of −ΔSm = 42.2 J kg-1 K-1 at 2 K for 7 T, which is higher than that of the commercial material, Gd3Ga5O12 (GGG), with −ΔSm of 38.4 J kg-1 K-1 under the same conditions. Moreover, the infrared spectrum (IR), UV-vis-NIR diffuse reflectance spectrum, and thermal stability were investigated.
AB - A single crystal of Sr14.06Gd14.63(BO3)24 has been successfully grown through a high-temperature solution technique with K2O-KF-B2O3 as the flux. It crystallizes in the Pnma space group with parameters a = 22.3153(5) Å, b = 15.9087(4) Å, c = 8.7507(2) Å, and Z = 2. Sr14.06Gd14.63(BO3)24 has a three-dimensional (3D) framework built from [GdO] chains, in which the isolate [BO3]3- groups and Sr2+ ions fill in the space of the 3D framework. The magnetic measurements revealed that the title compound exhibits a large magnetocaloric effect with the magnetic entropy change of −ΔSm = 42.2 J kg-1 K-1 at 2 K for 7 T, which is higher than that of the commercial material, Gd3Ga5O12 (GGG), with −ΔSm of 38.4 J kg-1 K-1 under the same conditions. Moreover, the infrared spectrum (IR), UV-vis-NIR diffuse reflectance spectrum, and thermal stability were investigated.
UR - https://www.scopus.com/pages/publications/85164230748
U2 - 10.1021/acs.inorgchem.3c01060
DO - 10.1021/acs.inorgchem.3c01060
M3 - Article
C2 - 37339514
AN - SCOPUS:85164230748
SN - 0020-1669
VL - 62
SP - 10263
EP - 10268
JO - Inorganic Chemistry
JF - Inorganic Chemistry
IS - 26
ER -