Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

Changhua An; Kaibin Tang; Bin Hai; Guozhen Shen; Chunrui Wang; Yitai Qian

doi:10.1016/S1387-7003(02)00707-4

Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

Changhua An
, Kaibin Tang^*
, Bin Hai
, Guozhen Shen
, Chunrui Wang
, Yitai Qian

^*此作品的通讯作者

University of Science and Technology of China

科研成果: 期刊稿件 › 文章 › 同行评审

28 引用（Scopus）

摘要

Monodispersed semiconducting SnTe nanocrystallites was successfully prepared via a solution synthesis route at room temperature. It was found that solvent (ethylenediamine), reductant (KBH₄), and tin source (liquid SnCl₄) were crucial factors in the preparation of the titled nanocrystals. X-ray powder diffraction (XRD), transmission electronic microscopy (TEM), X-ray photoelectron spectroscopy (XPS) were used to characterize the product. Raman spectrum of the as-prepared sample had a red shift by five or six wavenumbers in comparison with that of the SnTe single crystals.

源语言	英语
页（从-至）	181-184
页数	4
期刊	Inorganic Chemistry Communications
卷	6
期	2
DOI	https://doi.org/10.1016/S1387-7003(02)00707-4
出版状态	已出版 - 1 2月 2003
已对外发布	是

访问文件

10.1016/S1387-7003(02)00707-4

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{829c8083499d4e928a82a5b863544f68,

title = "Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature",

abstract = "Monodispersed semiconducting SnTe nanocrystallites was successfully prepared via a solution synthesis route at room temperature. It was found that solvent (ethylenediamine), reductant (KBH4), and tin source (liquid SnCl4) were crucial factors in the preparation of the titled nanocrystals. X-ray powder diffraction (XRD), transmission electronic microscopy (TEM), X-ray photoelectron spectroscopy (XPS) were used to characterize the product. Raman spectrum of the as-prepared sample had a red shift by five or six wavenumbers in comparison with that of the SnTe single crystals.",

keywords = "Nanocrystallites, Semiconducting, Solution synthesis, Telluride",

author = "Changhua An and Kaibin Tang and Bin Hai and Guozhen Shen and Chunrui Wang and Yitai Qian",

year = "2003",

month = feb,

day = "1",

doi = "10.1016/S1387-7003(02)00707-4",

language = "English",

volume = "6",

pages = "181--184",

journal = "Inorganic Chemistry Communications",

issn = "1387-7003",

publisher = "Elsevier B.V.",

number = "2",

}

TY - JOUR

T1 - Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

AU - An, Changhua

AU - Tang, Kaibin

AU - Hai, Bin

AU - Shen, Guozhen

AU - Wang, Chunrui

AU - Qian, Yitai

PY - 2003/2/1

Y1 - 2003/2/1

N2 - Monodispersed semiconducting SnTe nanocrystallites was successfully prepared via a solution synthesis route at room temperature. It was found that solvent (ethylenediamine), reductant (KBH4), and tin source (liquid SnCl4) were crucial factors in the preparation of the titled nanocrystals. X-ray powder diffraction (XRD), transmission electronic microscopy (TEM), X-ray photoelectron spectroscopy (XPS) were used to characterize the product. Raman spectrum of the as-prepared sample had a red shift by five or six wavenumbers in comparison with that of the SnTe single crystals.

AB - Monodispersed semiconducting SnTe nanocrystallites was successfully prepared via a solution synthesis route at room temperature. It was found that solvent (ethylenediamine), reductant (KBH4), and tin source (liquid SnCl4) were crucial factors in the preparation of the titled nanocrystals. X-ray powder diffraction (XRD), transmission electronic microscopy (TEM), X-ray photoelectron spectroscopy (XPS) were used to characterize the product. Raman spectrum of the as-prepared sample had a red shift by five or six wavenumbers in comparison with that of the SnTe single crystals.

KW - Nanocrystallites

KW - Semiconducting

KW - Solution synthesis

KW - Telluride

UR - https://www.scopus.com/pages/publications/0037293454

U2 - 10.1016/S1387-7003(02)00707-4

DO - 10.1016/S1387-7003(02)00707-4

M3 - Article

AN - SCOPUS:0037293454

SN - 1387-7003

VL - 6

SP - 181

EP - 184

JO - Inorganic Chemistry Communications

JF - Inorganic Chemistry Communications

IS - 2

ER -

Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

摘要

访问文件

其它文件与链接

学术指纹

引用此