Preparation of La0.9Sr0.1 Ga0.8Mg0.2O3-δ solid electrolyte for intermediate temperature by gel-combustion method

Nai Qing Zhang; Ke Ning Sun; Jin Hua Piao; Ning Ning Wu; De Rui Zhou

Preparation of La_0.9Sr_0.1 Ga_0.8Mg_0.2O_3-δ solid electrolyte for intermediate temperature by gel-combustion method

Nai Qing Zhang^*
, Ke Ning Sun
, Jin Hua Piao
, Ning Ning Wu
, De Rui Zhou

^*此作品的通讯作者

Harbin Institute of Technology

科研成果: 期刊稿件 › 文章 › 同行评审

3 引用（Scopus）

摘要

The solid electrolyte La_0.9Sr_0.1Ga_0.8 Mg_0.2O_3-δ (LSGM) was prepared by the gel-combustion method. The effects of technical parameters such as the concentration, the pH value, the amount of citrate added and heating temperature were discussed. The X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400°C for l0 h, and the TEM result shows the calcined powder with average particle size 150 nm.

源语言	英语
页（从-至）	758-761
页数	4
期刊	Rengong Jingti Xuebao/Journal of Synthetic Crystals
卷	33
期	5
出版状态	已出版 - 10月 2004
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{af0248ef122645d582945f3e9c07d2a9,

title = "Preparation of La0.9Sr0.1 Ga0.8Mg0.2O3-δ solid electrolyte for intermediate temperature by gel-combustion method",

abstract = "The solid electrolyte La0.9Sr0.1Ga0.8 Mg0.2O3-δ (LSGM) was prepared by the gel-combustion method. The effects of technical parameters such as the concentration, the pH value, the amount of citrate added and heating temperature were discussed. The X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400°C for l0 h, and the TEM result shows the calcined powder with average particle size 150 nm.",

keywords = "Gel-combustion, LaSrGaMgO, Solid electrolyte",

author = "Zhang, \{Nai Qing\} and Sun, \{Ke Ning\} and Piao, \{Jin Hua\} and Wu, \{Ning Ning\} and Zhou, \{De Rui\}",

year = "2004",

month = oct,

language = "English",

volume = "33",

pages = "758--761",

journal = "Rengong Jingti Xuebao/Journal of Synthetic Crystals",

issn = "1000-985X",

publisher = "Chinese Ceramic Society",

number = "5",

}

TY - JOUR

T1 - Preparation of La0.9Sr0.1 Ga0.8Mg0.2O3-δ solid electrolyte for intermediate temperature by gel-combustion method

AU - Zhang, Nai Qing

AU - Sun, Ke Ning

AU - Piao, Jin Hua

AU - Wu, Ning Ning

AU - Zhou, De Rui

PY - 2004/10

Y1 - 2004/10

N2 - The solid electrolyte La0.9Sr0.1Ga0.8 Mg0.2O3-δ (LSGM) was prepared by the gel-combustion method. The effects of technical parameters such as the concentration, the pH value, the amount of citrate added and heating temperature were discussed. The X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400°C for l0 h, and the TEM result shows the calcined powder with average particle size 150 nm.

AB - The solid electrolyte La0.9Sr0.1Ga0.8 Mg0.2O3-δ (LSGM) was prepared by the gel-combustion method. The effects of technical parameters such as the concentration, the pH value, the amount of citrate added and heating temperature were discussed. The X-ray diffraction characterization of calcined gel shows that pure phase was synthesized after calcination at 1400°C for l0 h, and the TEM result shows the calcined powder with average particle size 150 nm.

KW - Gel-combustion

KW - LaSrGaMgO

KW - Solid electrolyte

UR - https://www.scopus.com/pages/publications/10444242533

M3 - Article

AN - SCOPUS:10444242533

SN - 1000-985X

VL - 33

SP - 758

EP - 761

JO - Rengong Jingti Xuebao/Journal of Synthetic Crystals

JF - Rengong Jingti Xuebao/Journal of Synthetic Crystals

IS - 5

ER -

Preparation of La0.9Sr0.1 Ga0.8Mg0.2O3-δ solid electrolyte for intermediate temperature by gel-combustion method

摘要

其它文件与链接

学术指纹

引用此

Preparation of La_0.9Sr_0.1 Ga_0.8Mg_0.2O_3-δ solid electrolyte for intermediate temperature by gel-combustion method