TY - GEN
T1 - Preparation of epoxy resin composites by chitosan modified montmorillonite
AU - Chen, Ying
AU - Xie, Jing
AU - Shen, Shangyue
AU - Jin, Ping
PY - 2011
Y1 - 2011
N2 - OMMT was compounded by MMT and 1% (v/v) acetic acid dissolved chitosan via solution intercalate method, and then prepared the composites with epoxy resin. The change about spacing of montmorillonite was tested by XRD, and the molecular structure of OMMT was tested by Fourier infrared spectrum. The tensile strength and impact strength of epoxy resin composites were also tested. The result showed that the spacing of montmorillonite first increased then decreased along with the increasing mass fraction of chitosan. The maximum value (d 001=1.983 nm) appeared when mass fraction of chitosan was 30%. And tensile strength and impact strength were improved by 86.8 and 51.2% respectively.
AB - OMMT was compounded by MMT and 1% (v/v) acetic acid dissolved chitosan via solution intercalate method, and then prepared the composites with epoxy resin. The change about spacing of montmorillonite was tested by XRD, and the molecular structure of OMMT was tested by Fourier infrared spectrum. The tensile strength and impact strength of epoxy resin composites were also tested. The result showed that the spacing of montmorillonite first increased then decreased along with the increasing mass fraction of chitosan. The maximum value (d 001=1.983 nm) appeared when mass fraction of chitosan was 30%. And tensile strength and impact strength were improved by 86.8 and 51.2% respectively.
KW - Chitosan
KW - Epoxy resin composites
KW - Organic montmorillonite
UR - https://www.scopus.com/pages/publications/80053045304
U2 - 10.4028/www.scientific.net/AMR.311-313.113
DO - 10.4028/www.scientific.net/AMR.311-313.113
M3 - Conference contribution
AN - SCOPUS:80053045304
SN - 9783037852149
T3 - Advanced Materials Research
SP - 113
EP - 116
BT - Advanced Materials and Processes
T2 - 2011 International Conference on Advanced Design and Manufacturing Engineering, ADME 2011
Y2 - 16 September 2011 through 18 September 2011
ER -