Direct precipitation method of Nano-CuO

Mingyu Li; Kefu Ding; Zhihao Li; Zeng Qingxuan

doi:10.1051/matecconf/201710802003

Direct precipitation method of Nano-CuO

Mingyu Li^*
, Kefu Ding
, Zhihao Li
, Zeng Qingxuan

^*此作品的通讯作者

机电学院

Beijing Institute of Technology

科研成果: 期刊稿件 › 会议文章 › 同行评审

1 引用（Scopus）

摘要

Different reaction conditions were studied through orthogonal experiment and single factor experiment. Using Cu(NO3)2 as the reactant, water-Alcohol solution (H2O:CH2CH3OH was 3:1) as solvent at 20°C and reaction for 45min could get nano-CuO with good dispersion and uniform size. Different kinds of characterization method were used to characterize the resultant. The average diameter of nano-CuO was 20.38nm after calculated using some relevant formula, the surface area was about 21.988 m2/g, the pore diameter was about 3.079 nm and the pore volume was 1.349×10-1 cc/g. So the method is a feasible, low cost way to industry.

源语言	英语
期刊论文编号	02003
期刊	MATEC Web of Conferences
卷	108
DOI	https://doi.org/10.1051/matecconf/201710802003
出版状态	已出版 - 31 5月 2017
活动	2017 International Conference on Mechanical, Aeronautical and Automotive Engineering, ICMAA 2017 - Malacca, 马来西亚期限: 25 2月 2017 → 27 2月 2017

访问文件

10.1051/matecconf/201710802003

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{ee40e6ee7ac648aa961b55c21a604f10,

title = "Direct precipitation method of Nano-CuO",

abstract = "Different reaction conditions were studied through orthogonal experiment and single factor experiment. Using Cu(NO3)2 as the reactant, water-Alcohol solution (H2O:CH2CH3OH was 3:1) as solvent at 20°C and reaction for 45min could get nano-CuO with good dispersion and uniform size. Different kinds of characterization method were used to characterize the resultant. The average diameter of nano-CuO was 20.38nm after calculated using some relevant formula, the surface area was about 21.988 m2/g, the pore diameter was about 3.079 nm and the pore volume was 1.349{\texttimes}10-1 cc/g. So the method is a feasible, low cost way to industry.",

author = "Mingyu Li and Kefu Ding and Zhihao Li and Zeng Qingxuan",

note = "Publisher Copyright: {\textcopyright} The Authors, published by EDP Sciences, 2017.; 2017 International Conference on Mechanical, Aeronautical and Automotive Engineering, ICMAA 2017 ; Conference date: 25-02-2017 Through 27-02-2017",

year = "2017",

month = may,

day = "31",

doi = "10.1051/matecconf/201710802003",

language = "English",

volume = "108",

journal = "MATEC Web of Conferences",

issn = "2261-236X",

publisher = "EDP Sciences",

}

TY - JOUR

T1 - Direct precipitation method of Nano-CuO

AU - Li, Mingyu

AU - Ding, Kefu

AU - Li, Zhihao

AU - Qingxuan, Zeng

PY - 2017/5/31

Y1 - 2017/5/31

N2 - Different reaction conditions were studied through orthogonal experiment and single factor experiment. Using Cu(NO3)2 as the reactant, water-Alcohol solution (H2O:CH2CH3OH was 3:1) as solvent at 20°C and reaction for 45min could get nano-CuO with good dispersion and uniform size. Different kinds of characterization method were used to characterize the resultant. The average diameter of nano-CuO was 20.38nm after calculated using some relevant formula, the surface area was about 21.988 m2/g, the pore diameter was about 3.079 nm and the pore volume was 1.349×10-1 cc/g. So the method is a feasible, low cost way to industry.

AB - Different reaction conditions were studied through orthogonal experiment and single factor experiment. Using Cu(NO3)2 as the reactant, water-Alcohol solution (H2O:CH2CH3OH was 3:1) as solvent at 20°C and reaction for 45min could get nano-CuO with good dispersion and uniform size. Different kinds of characterization method were used to characterize the resultant. The average diameter of nano-CuO was 20.38nm after calculated using some relevant formula, the surface area was about 21.988 m2/g, the pore diameter was about 3.079 nm and the pore volume was 1.349×10-1 cc/g. So the method is a feasible, low cost way to industry.

UR - https://www.scopus.com/pages/publications/85020434458

U2 - 10.1051/matecconf/201710802003

DO - 10.1051/matecconf/201710802003

M3 - Conference article

AN - SCOPUS:85020434458

SN - 2261-236X

VL - 108

JO - MATEC Web of Conferences

JF - MATEC Web of Conferences

M1 - 02003

T2 - 2017 International Conference on Mechanical, Aeronautical and Automotive Engineering, ICMAA 2017

Y2 - 25 February 2017 through 27 February 2017

ER -

Direct precipitation method of Nano-CuO

摘要

访问文件

其它文件与链接

学术指纹

引用此