Degradation behavior of electrochemical performance of sealed-type nickel/metal hydride batteries

The degradation mechanism of electrochemical performance of sealed-type nickel/metal hydride batteries was investigated. The results indicate that the degradation behavior of Ni/MH battery is not only owing to the lack of electrolyte, but also the deterioration of the active materials on the positive and negative electrodes of Ni/MH batteries. Scanning electron micrographs (SEM), X-ray diffraction (XRD) and laser granularity analyses are presented. The particle pulverization and oxidation during charge/discharge are identified as the main causes for deterioration of the negative and positive electrode in nickel/metal hydride batteries, as well as the cross-section cracking of both anode and cathode.