A nanoscale core-shell of β-SiCP-Ni prepared by electroless plating at lower temperature

Gui Zhen Zou; Mao Sheng Cao; Liang Zhang; Jin Gang Li; Hui Xu; Yu Jin Chen

doi:10.1016/j.surfcoat.2005.11.026

A nanoscale core-shell of β-SiC_P-Ni prepared by electroless plating at lower temperature

Gui Zhen Zou
, Mao Sheng Cao^*
, Liang Zhang
, Jin Gang Li
, Hui Xu
, Yu Jin Chen

^*此作品的通讯作者

材料学院

Beijing Institute of Technology
CAS - Institute of Physics

科研成果: 期刊稿件 › 文章 › 同行评审

58 引用（Scopus）

摘要

A nanoscale core-shell structure of β-SiC_P-Ni was prepared at lower temperature by a simple and convenient electroless plating approach. The core-shell structure was characterized by means of SEM, TEM images and the components were analyzed using EDS. The results showed that β-SiC nanoparticles (β-SiC_P) were coated by an uniform and continuous nickel shell with the thickness of 2 nm. Moreover, it was confirmed that the optimal temperature and the solution pH value for electroless plating were of 45 °C and 9.0, respectively. The mechanism for the formation of the core-shell structure of β-SiC_P-Ni was discussed in detail.

源语言	英语
页（从-至）	108-112
页数	5
期刊	Surface and Coatings Technology
卷	201
期	1-2
DOI	https://doi.org/10.1016/j.surfcoat.2005.11.026
出版状态	已出版 - 12 9月 2006

访问文件

10.1016/j.surfcoat.2005.11.026

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{16ff3adfe39f4932a3b4e088ccce0682,

title = "A nanoscale core-shell of β-SiCP-Ni prepared by electroless plating at lower temperature",

abstract = "A nanoscale core-shell structure of β-SiCP-Ni was prepared at lower temperature by a simple and convenient electroless plating approach. The core-shell structure was characterized by means of SEM, TEM images and the components were analyzed using EDS. The results showed that β-SiC nanoparticles (β-SiCP) were coated by an uniform and continuous nickel shell with the thickness of 2 nm. Moreover, it was confirmed that the optimal temperature and the solution pH value for electroless plating were of 45 °C and 9.0, respectively. The mechanism for the formation of the core-shell structure of β-SiCP-Ni was discussed in detail.",

keywords = "Core-shell, Electroless plating, Nanoparticle, Quasi-monoparticles layer, Silicon carbide (SiC), Surface decoration",

author = "Zou, \{Gui Zhen\} and Cao, \{Mao Sheng\} and Liang Zhang and \{Gang Li\}, Jin and Hui Xu and Chen, \{Yu Jin\}",

year = "2006",

month = sep,

day = "12",

doi = "10.1016/j.surfcoat.2005.11.026",

language = "English",

volume = "201",

pages = "108--112",

journal = "Surface and Coatings Technology",

issn = "0257-8972",

publisher = "Elsevier B.V.",

number = "1-2",

}

TY - JOUR

T1 - A nanoscale core-shell of β-SiCP-Ni prepared by electroless plating at lower temperature

AU - Zou, Gui Zhen

AU - Cao, Mao Sheng

AU - Zhang, Liang

AU - Gang Li, Jin

AU - Xu, Hui

AU - Chen, Yu Jin

PY - 2006/9/12

Y1 - 2006/9/12

N2 - A nanoscale core-shell structure of β-SiCP-Ni was prepared at lower temperature by a simple and convenient electroless plating approach. The core-shell structure was characterized by means of SEM, TEM images and the components were analyzed using EDS. The results showed that β-SiC nanoparticles (β-SiCP) were coated by an uniform and continuous nickel shell with the thickness of 2 nm. Moreover, it was confirmed that the optimal temperature and the solution pH value for electroless plating were of 45 °C and 9.0, respectively. The mechanism for the formation of the core-shell structure of β-SiCP-Ni was discussed in detail.

AB - A nanoscale core-shell structure of β-SiCP-Ni was prepared at lower temperature by a simple and convenient electroless plating approach. The core-shell structure was characterized by means of SEM, TEM images and the components were analyzed using EDS. The results showed that β-SiC nanoparticles (β-SiCP) were coated by an uniform and continuous nickel shell with the thickness of 2 nm. Moreover, it was confirmed that the optimal temperature and the solution pH value for electroless plating were of 45 °C and 9.0, respectively. The mechanism for the formation of the core-shell structure of β-SiCP-Ni was discussed in detail.

KW - Core-shell

KW - Electroless plating

KW - Nanoparticle

KW - Quasi-monoparticles layer

KW - Silicon carbide (SiC)

KW - Surface decoration

UR - https://www.scopus.com/pages/publications/33745960372

U2 - 10.1016/j.surfcoat.2005.11.026

DO - 10.1016/j.surfcoat.2005.11.026

M3 - Article

AN - SCOPUS:33745960372

SN - 0257-8972

VL - 201

SP - 108

EP - 112

JO - Surface and Coatings Technology

JF - Surface and Coatings Technology

IS - 1-2

ER -

A nanoscale core-shell of β-SiCP-Ni prepared by electroless plating at lower temperature

摘要

访问文件

其它文件与链接

学术指纹

引用此

A nanoscale core-shell of β-SiC_P-Ni prepared by electroless plating at lower temperature